Using Garfield, Washington, nontronite as the model mineral system, methods and apparatus were developed to prepare reduced suspensions in citrate-bicarbonate-dithionite (CBD) solution. These techniques were effective in removing excess, undesired solutes from reduced suspensions while maintaining a high Fe2+ content. They also enabled the preparation of dried, reduced films preferentially oriented with respect to the crystallographic c-axis. Supernatant solutions were collected and analyzed for Fe, Al, and Si, from which the extent of dissolution of the clay as a result of CBD treatment was assessed. Results indicated that very little Fe and Si were released to solution, but as much as about 8% of the total Al was solubilized. The highest levels of Al in solution were observed in CB treatments without dithionite.

The effects of reduction and reoxidation of octahedral Fe3+ on the exchange of structural hydrogen in nontronite were determined using tritium (3H) as a label element. The uptake of H from the surrounding solution of nontronite suspensions increased as the reduction of structural Fe3+ increased. Similarly, the loss of H from the structure increased as the reduction increased. The results are generally consistent with a reduction mechanism involving the loss of structural OH, leaving the affected Fe sites with less than six-fold coordination. The attenuation of increased negative charge on the clay layer, however, was less than predicted by such a mechanism.

During the reoxidation of reduced nontronite in suspension, about one-third of the H remaining as part of the structure following reduction was lost, whereas twice that amount of H was incorporated into the structure from the surrounding solution. A reoxidation mechanism is proposed whereby H2O from the surrounding solution is incorporated into the mineral structure followed by the elimination of a hydrogen ion, returning the Fe to six-fold coordination. This mechanism implies the reversibility of Fe reduction in nontronite.

Iron impurities in the Hohen Hagen nontronite (NG-1) were identified as maghemite and goethite. The phase identified as maghemite was magnetically ordered at both room temperature and 87 K, with hyperfine magnetic fields of 48.6 and 50.7 tesla, respectively. Due to the magnetic properties of this phase, it was easily separated from aqueous dispersions of the clay using a hand magnet. X-ray powder diffraction analysis revealed maghemite, quartz, and phyllosilicate in the magnetically separated phase. The impurity identified as goethite remained in the non-magnetic <2-μm fraction of the clay, displayed magnetic order only at 87 K (47.44 tesla hyperfine field), and accounted for about 8% of the total area of the Mössbauer spectrum.

The effect of Fe oxidation state on the specific surface area, Sm, of nontronite was studied using the <2-µm, Na+-saturated fraction of the SWa-1 and Garfield nontronite reference clays. The reduction of structural Fe3+ in the octahedral sheet of the nontronite decreased Sm as measured by the adsorption of 2-ethoxyethanol (ethylene glycol-monoethyl ether, EGME). The swellability in water of the nontronite also decreased during reduction. The amount of nonexchangeable Na+, on the other hand, increased with increasing Fe2+ content and was highly correlated with EGME adsorption (r = -.985). The relationship between Sm and Fe2+ was attributed to the collapse of partially or fully expanded layers to unexpanded layers.

The reduction and reoxidation of three nontronite samples, GAN (API H-33a, Garfield, Washington), SWa-1 (ferruginous Washington smectite), and NG-1 (Hohen Hagen, Federal Republic of Germany) were studied with visible absorption and Mössbauer spectroscopy. The intensity of the intervalence electron transfer (IT) band at 730 nm in these nontronites was monitored during reduction and reoxidation at 277, 294, and 348 K. The results showed that the intensity of the band followed the number of Fe(II)-O-Fe(III) groups in the clay crystal, increasing to a maximum at about Fe(II): total Fe = 0.4; upon complete reduction, the band decreased to about the intensity of the unaltered, oxidized sample. With reoxidation of the sample with O2, the intensity of the band increased sharply, followed by a gradual decay back to the original, oxidized intensity. The ultimate level of Fe reduction achieved was at least 92%. Concomitantly, the color changed from yellow through green, blue-green, dark blue, light blue, and light gray as the Fe(II) content increased. The GAN nontronite was more difficult to reduce than the SWa-1 or NG-1 samples. The rate and level of reduction increased with the amount of reducing agent added.

The effects of chemical reduction of structural Fe3+ in nontronite SWa-1 (ferruginous smectite) on intervalence electron transfer (IT) and magnetic exchange were investigated. Visible absorption spectra in the region 800-400 nm of a chemical reduction series of the SWa-1 nontronite revealed an IT band near 730 nm (13,700 cm−1). Both the intensity and position of this band were affected by the extent of Fe reduction. The intensity increased until the Fe2+ content approached 40% of the total Fe, then decreased slightly with more Fe2+. The position of the band also shifted to lower energy as the extent of reduction increased.

Variable-temperature magnetic susceptibility measurements showed that the magnetic exchange in unaltered nontronite is frustrated antiferromagnetic, but ferromagnetic in reduced samples. Magnetic ordering temperatures are in the range 10–50 K, depending on the extent of reduction. The ferromagnetic component in the magnetization curve increased with increasing Fe2+ in the crystal structure. The positive paramagnetic interaction likely is due to electron charge transfer from Fe2+ to Fe3+ through such structural linkages as Fe2+-O-Fe3+ (perhaps following a double exchange mechanism), which is consistent with the visible absorption spectra.

Aqueous gels of unaltered (oxidized) and chemically reduced ferruginous smectite (SWa-1 from the Source Clays Repository of The Clay Minerals Society) were characterized by transmission electron microscopy, electron diffraction, and energy-dispersive X-ray fluorescence to establish details regarding their texture, inter-layer and inter-particle arrangements, and chemical composition. Micrographs revealed that the reduction of structural Fe(III) to Fe(II) caused a consolidation of smectite particles from an extensive network of small crystals (1–6 layers thick) to distinct particles of limited size in the a-b direction and about 20–40 layers thick. The interlayer distances in the reduced sample appeared to be more uniform than in the oxidized sample, but both exhibited spacings of about 12.6 A. Chemical analysis showed no qualitative differences as a result of oxidation state. Electron diffraction patterns displayed marked differences. The pattern of the oxidized sample consisted of homogeneous rings, indicating that the stacking order in the a-b plane was turbostratic or disordered, whereas the reduced pattern exhibited much more order as evidenced by distinct spots amid low-intensity rings, suggesting that inter-layer attractive forces were stronger if Fe(II) was present in the clay crystal.

Three montmorillonites and a nontronite were reduced by sodium dithionite to obtain different amounts of Fe2+ in their octahedral sites. The mass ratio of water to clay, mw/mc was determined as a function of Fe2+ at several values of the swelling pressure, π. The value mwmc decreased markedly with increasing Fe2+ at each value of π for each clay. Moreover, curves of π vs. mwmc for the different clays were displaced downwards as Fe2+ increased. A straight line was obtained when In(π + 1) was plotted against 1/(mw/mc) however, at some oxidation states of three of the samples this line exhibited a sharp break at a specific value of 1/(w/mc. The slope of the line decreased for each clay as Fe2+ increased, and an increase in Fe2+ was accompanied by an increase in the cation exchange capacity. These observations are thought to be due to a collapse or partial collapse of the superimposed clay layers resulting from the increase in cation-exchange capacity.

The effect of Fe oxidation state on the surface charge (CEC) and solubility of smectites were studied using the <2-μm, Na+-saturated fraction of an Upton, Wyoming; a Czechoslovakian; and a New Zealand montmorillonite; and a Garfield, Washington, nontronite. The reduction of structural Fe3+ in the octahedral sheet of each clay produced a net increase in the negative surface charge of the clay. The observed cation-exchange capacities deviated from the linear relationship predicted by charge-deficit calculations, assuming changes only in the Fe2+/Fe3+ ratio, and reversibly followed Fe reduction according to a 2nd-degree polynomial function. The deviations suggest reversible changes in mineral structure and composition during Fe reduction.

These clays were susceptible to partial dissolution in citrate bicarbonate (CB) and citrate-bicarbonate-dithionite (CBD) solutions. Small amounts of Fe and Si dissolved as a result of Fe reduction in CBD, but affected <1% of the total clay mass except for the Czechoslovakian clay in which 2% of the clay dissolved. Although slightly more Fe dissolved than Si, no change in surface charge was noted. Almost no dissolution of these elements was detected in CB solution. In contrast, significant Al was detected in the CB solution, suggesting a heterogeneous dissolution mechanism. The CEC, however, was unchanged by the CB treatment. These results may be explained by the adsorption of hydrogen ions into the vacated Al3+ sites in the mineral structure. Dissolution seems to have been independent of the effects of Fe oxidation state on surface charge.

Shewanella putrefaciens is a species of metal-reducing bacteria with a versatile respiratory metabolism. This study reports that S. putrefaciens strain MR-1 rapidly reduces Fe(III) within smectite clay minerals. Up to 15% of the structural Fe within ferruginous smectite (sample SWa-1, Source Clays Repository of the Clay Minerals Society) was reduced by MR-1 in 4 h, and a range of 25% to 41% of structural Fe was reduced after 6 to 12 d during culture. Conditions for which smectite reduction was optimal, that is, pH 5 to 6, at 25 to 37 °C, are consistent with an enzymatic process and not with simple chemical reduction. Smectite reduction required viable cells, and was coupled to energy generation and carbon metabolism for MR-1 cultures with smectite added as the sole electron acceptor. Iron(III) reduction catalyzed by MR-1 was inhibited under aerobic conditions, and under anaerobic conditions it was inhibited by the addition of nitrate as an alternate electron acceptor or by the metabolic inhibitors tetrachlorosali-cylanilide (TCS) or quinacrine hydrochloride. Genetic mutants of MR-1 deficient in anaerobic respiration reduced significantly less structural Fe than wild-type cells. In a minimal medium with formate or lactate as the electron donor, more than three times the amount of smectite was reduced over no-carbon controls. These data point to at least one mechanism that may be responsible for the microbial reduction of clay minerals within soils, namely, anaerobic respiration, and indicate that pure cultures of MR-1 provide an effective model system for soil scientists and mineralogists interested in clay reduction. Given the ubiquitous distribution and versatile metabolism of MR-1, these studies may have further implications for bioremediation and water quality in soils and sediments.

Partial stabilization of Fe(II) in chemically reduced smectite, which normally readily undergoes reoxidation in air, was achieved. The purpose of this study was to determine if Fe(II) can be stabilized in reduced smectites by Li fixation upon heating. More than 80% of total Fe in ferruginous smectite SWa-1 was reduced to Fe(II) using the citrate-bicarbonate-dithionite (CBD) method while purging the clay dispersion with N2. The reduced smectite was Li-saturated, washed free of excess ions, freeze-dried, and heated in N2 atmosphere at 260°C for 24 h to produce Li-fixation. This treatment caused partial stabilization of Fe(II) in the clay structure. Chemical analysis, Mössbauer spectroscopy, and Fourier transform infrared (FTIR) spectroscopy proved that <20% of total Fe was Fe(II) after reoxidation with oxygen in a water dispersion, a treatment which causes complete reoxidation of Fe(II) in reduced Na-smectites. Decomposition of the OH-stretching band evident in the IR spectra indicated migration of Li into the vacant octahedra. Some of the OH groups in the reoxidized smectite were found in local trioctahedral configurations, associated with the AlFe(II)Li or Fe(III)Fe(II)Li groupings of central atoms in the octahedral sheet.

Reduction of structural Fe in Na-exchanged dioctahedral smectites decreases swellability in water, but because clay interlayers also collapse in the process the concomitant effect on surface hydration energy is uncertain. This study examined the hydration behavior of oxidized and reduced dioctahedral smectite clays exchanged with polar (Na) and weakly-polar (organic) cations to determine the nature of the surface before and after Fe reduction, and to determine if clay surfaces are hydrophilic or hydrophobic. The H2O content in various dioctahedral smectites decreased if Na was replaced by tetramethylammonium (TMA), trimethylphenylammonium (TMPA), or hexadecyltrimethylammonium (HDTMA). Among the organo-clays, H2O adsorption decreased with increasing complexity of the cation. For oxidized smectites, those exchanged with TMPA retained less H2O than those exchanged with Na at all pressures. The extent of this difference depended on the clay and decreased with increasing applied pressure. Reduction of Fe(III) to Fe(II) in the octahedral sheets decreased the swelling of Na-saturated smectites, apparently causing some previously swelling interlayers to collapse. If the Na interlayer cation was exchanged to alkylammonium after reduction, but prior to swelling-pressure measurements, the swelling increased or remained near constant, suggesting that the organo-cation disrupted the collapse process of the interlayers associated with the reduced smectite layers. Reduced TMPA-saturated smectite surfaces are more strongly hydrated if the octahedral sheet is reduced than if oxidized. Thus, reduction of structural Fe increases the hydration energy of smectite basal surfaces, but swellability could decrease or increase depending on the extent of interlayer collapse occurring with different exchangeable cations.

Redox cycles are common in nature and likely have a profound effect on the behavior of soils and sediments. This study examined a key component of redox cycles in smectites, namely, the reoxidation process, which has received little attention compared to the reduction process. Unaltered (oxidized) and reoxidized ferruginous smectites (nontronites) were compared using infrared and Mössbauer spectroscopies, and thermal gravimetric analysis. The infrared and thermal gravimetric data revealed that the structural OH content of reduced-reoxidized clay is about 15 to 20% less than in the original (oxidized) sample, indicating that the structure remains partially dehydroxylated even after reoxidation. Mössbaner spectra of reoxidized samples consisted of larger quadrupole splitting for Fe(III) doublets than in the unaltered samples, suggesting that the environment of Fe(III) is more distorted after the reduction-reoxidation treatment.

Microbial reduction of clay mineral structural Fe(III) decreases the swelling of nontronite gels, most importantly at intermediate oxidation states (40 to 80 cmol Fe(II) kg−1 clay). The purpose of this study was to establish whether microbial reduction of structural Fe(III) decreased the swelling of other Fe-bearing smectites and to discern the influence that organic compounds of microbial origin (bacterial cells, cell fragments and/or exudates) may have on clay swelling and texture. Structural Fe(III) was reduced by incubating smectite suspensions with either a combination of Pseudomonas bacteria or a mixture of anaerobic bacteria. The influence of organics on clay swelling was estimated on smectites suspended in either organic or inorganic media in the absence of bacteria. The gravimetric water content of the reduced clay gels equilibrated at various applied pressures was recorded as a function of Fe oxidation state. Transmission electron microscopy (TEM) was employed to determine the influence of bacteria and type of media on the texture of reduced smectite gels. Reduction of structural Fe(III) by bacteria decreased the swelling pressure of all Fe-bearing smectites. Increased clay swelling, due to the presence of organics (organic medium, exudates or cell fragments), was correlated to the total Fe content, the extent of structural Fe reduction, as well as the initial swelling characteristics of the Fe-bearing smectites. High structural Fe(II) contents (>50 cmol Fe(II) kg−1) resulted in increased attractive forces between clay platelets that decreased clay swelling, even in organic medium suspensions. Microbial reduction resulted in increased face-face association of individual clay layers, forming larger and more distinct crystallite subunits than in nonreduced clay gels. But, perhaps more importantly, microbial reduction of structural Fe(III) resulted in an increased association between crystallite subunits and, thus, an overall larger particle size and pore size distribution, due to the interaction of bacteria ceils, cell fragments and organic exudates.

The oxidation state of structural Fe greatly alters surface chemistry, which may have a large influence on clay-organic interactions. The effect of structural-iron oxidation state on chlorinated hydrocarbons at the clay-water interface was examined. Pentachloroethane (5CA) was reacted with oxidized, reduced, and reoxidized forms of three different smectites: montmorillonite, ferruginous smectite, and nontronite in aqueous suspension under controlled-atmosphere conditions. Pentachloroethane was found to adsorb at different rates for the three smectites. A series of 5CA-adsorption rate constants in the presence of these clays showed a strong correlation with the Fe(II) content of the clay (r2 = 0.98). The clay surface behaves as a Brønsted base and promotes 5CA dehydrochlorination. The adsorption kinetics at the clay-water interface were described by the formation of a precursor complex prior to 5CA dehydrochlorination.

The long-term impermeability of clay barriers in waste disposal facilities and hydraulic structures is of critical importance to environmental, agricultural, and industrial concerns. Changes in the oxidation state of Fe in the constituent clays of compacted clay barriers may degrade the hydraulic conductivity of these structures because other properties related to hydraulic conductivity, such as swelling, gel microstructure, and particle size, are greatly altered by the oxidation state. Two Na-saturated smectites (SWa-1 and API 25) were reduced by sodium dithionite (Na2S2O4), both in suspension and in situ after consolidation, to examine the effects of structural Fe reduction on hydraulic conductivity. Results indicated that the hydraulic conductivity depended on both the oxidation state and the consolidation history of the clay. The hydraulic conductivity of clay reduced in suspension before consolidation was lower than that of oxidized clay. Initially reduced smectite, thus, may be compactable to a less-permeable material with higher bulk density. But reduction of smectite in situ after consolidation increased the hydraulic conductivity and its variability. The oxidized state of clay liners should, therefore, be preserved.

The oxidation state of structural iron greatly influences the physical-chemical properties of clay minerals, a phenomenon that may have significant implications for pollutant fate in the environment, for agricultural productivity, and for industrial uses of clays. Knowledge of redox mechanisms is fundamental to understanding the underlying basis for iron's effects on clays. Past studies revealed that the extent of Fe reduction varied depending on the reducing agent used, but this variation may not have been a simple function of the reduction potential of the reducing agent. The objective of this study was to identify the relationship between the Fe reduction mechanism and free radical activity in the reducing agent. Several reducing agents and their mixtures with the Na-saturated, 0.5 to 2 μm size fraction of ferruginous smectite (SWa-1) were analyzed by electron spin resonance (ESR) spectroscopy to determine the presence of unpaired electrons or free radicals. Only Na2S2O4 exhibited paramagnetic free-radical behavior with a signal at about g = 2.011, which was attributed to the sulphoxylate (S02− ·) free radical. The free radical was labile in aqueous solution, and the ability of Na2S2O4 solution to reduce structural Fe in the smectite decreased with age of the solution and paralleled the disappearance of the free radical signal in the ESR spectrum. The paramagnetic species was preserved and enhanced if Na2S2O4 was added to the clay suspension, indicating that either the clay surface stabilized the SO2− · radical or the additional unpaired electrons were produced in the clay structure.