A recent report on the “room temperature superplasticity” in the Zr64.13Cu15.75Ni10.12Al10 bulk metallic glass [Y.H. Liu et al., Science315, 1385 (2007)] was ascribed to the distinctive micrometer-sized structural heterogeneity. To verify the microstructure in this alloy, transmission electron microscopy (TEM) and anomalous small-angle x-ray scattering experiments were conducted. The results show that no micrometer-sized or nanometer-sized structural heterogeneities can be found. The micrometer-sized dark and bright regions that were previously reported as the reason for the plasticity are artifacts caused by TEM specimen preparation, rather than the intrinsic structure feature of this alloy. This finding is important for further studying the unique properties of this alloy.

A Yb:KGW femtosecond laser (400 fs) with 3rd and 4th harmonic generators (wavelength = 343 and 258 nm) was adopted to a locally built 3DAP instrument to assist field evaporation from ceramics tips that were bonded on tungsten wire. Using this setting, we have demonstrated that quantitative atom probe tomography is possible from Y2O3-ZrO2-MgAl2O4, (Ce,Y)O2, Li(Co,Ni,Mg,Al)O2 sintered bulk ceramics, which are all insulators.