Constraint Effects on Thin Film Channel Cracking Behavior

  • Ting Y. Tsui (a1), Andrew J. McKerrow (a1) and Joost J. Vlassak (a2)
Abstract

One of the most common forms of cohesive failure observed in brittle thin film subjected to a tensile residual stress is channel cracking, a fracture mode in which through-film cracks propagate in the film. The crack growth rate depends on intrinsic film properties, residual stress, the presence of reactive species in the environments, and the precise film stack. In this paper, we investigate the effect of various buffer layers sandwiched between a brittle carbon-doped-silicate (CDS) film and a silicon substrate on channel cracking of the CDS film. The results show that channel cracking is enhanced if the buffer layer is more compliant than the silicon substrate. Crack velocity increases with increasing buffer layer thickness and decreasing buffer layer stiffness. This is caused by a reduction of the constraint imposed by the substrate on the film and a commensurate increase in energy release rate. The degree of constraint is characterized experimentally as a function of buffer layer thickness and stiffness, and compared to the results of a simple shear lag model that was proposed previously. The results show that the shear lag model does not accurately predict the effect of the buffer layer.

Copyright
Corresponding author
a) Address all correspondence to this author. e-mail: ttsui@ti.com This paper was selected as the Outstanding Meeting Paper for the 2005 MRS Spring Meeting Symposium B Proceedings, Vol. 863.
Linked references
Hide All

This list contains references from the content that can be linked to their source. For a full set of references and notes please see the PDF or HTML where available.

3T.Y. Tsui , A.J. Griffin Jr., J. Jacques , R. Fields , A.J. McKerrow , and R. Kraft : Effects of elastic modulus on the fracture behavior of low-dielectric constant films, in Proceedings of the 2005 IEEE International Interconnect Technology Conference (IEEE Electronic Devices Society, Piscataway, NJ, 2005), pp. 6365.

4A.A. Volinsky , P. Waters , J.D. Kiely and E. Johns : Sub-critical telephone cord delamination propagation, in Stability of Thin Films and Nanostructures, edited by R.P. Vinci , R. Schwaiger , A. Karim , and V. Shenoy (Mater. Res. Soc. Symp. Proc. 854E, Warrendale, PA, 2004), U9.5.

6R.F. Cook and E.G. Liniger : Stress-corrosion cracking of low-dielectric-constant spin-on-glass thin films. J. Electrochem. Soc. 146, 4439 (1999).

7J.L. Beuth Jr.: Cracking of thin bonded films in residual tension. Int. J. Solids Struct. 29, 1657 (1992).

8J. Dundurs : Edge-bonded dissimilar orthogonal elastic wedges. J. Appl. Mech. 36, 650 (1969).

10S.M. Wiederhorn and H. Johnson : Effect of electrolyte pH on crack propagation in glass. J. Am. Ceram. Soc. 56(4), 192 (1973).

13J. He , G. Xu and Z. Suo Experimental determination of crack driving forces in integrated structures, in Proceedings of the 7th International Workshop on Stress-Induced Phenomena in Metallization, edited by P.S.W. Ho , S.P. Baker , T. Nakamura , and C.A. Volkert (American Institute of Physics, New York, 2004), pp. 314.

Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Journal of Materials Research
  • ISSN: 0884-2914
  • EISSN: 2044-5326
  • URL: /core/journals/journal-of-materials-research
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords: