Biomagnetic field sensors based on AlN/FeCoSiB magnetoelectric (ME) composites desire a resonant frequency that can be precisely tuned to match the biomagnetic signal of interest. A tunable mechanical resonant frequency is achieved when ME composites are integrated onto shape memory alloy (SMA) thin films. Here, high-quality c-axis growth of AlN is obtained on (111) Pt seed layers on both amorphous and crystallized TiNiCu SMA thin films on Si substrates. These composites show large piezoelectric coefficients as high as d33,f= 6.4 pm/V ± 0.2 pm/V. Annealing the AlN/Pt/Ta/amorphous TiNiCu/Si composites to 700 °C to crystallize TiNiCu promoted interdiffusion of Ti into the Ta/Pt layers, leading to an enhanced conductivity in AlN. Depositing AlN onto already crystalline TiNiCu films with low surface roughness resulted in the best piezoelectric films and hence is found to be a more desirable processing route for ME composite applications.

In situ transmission electron microscope (TEM) characterization techniques provide valuable information on structure–property correlations to understand the behavior of materials at the nanoscale. However, understanding nanoscale structures and their interaction with the electron beam is pivotal for the reliable interpretation of in situ/ex situ TEM studies. Here, we report that oxides commonly used in nanoelectronic applications, such as transistor gate oxides or memristive devices, are prone to electron beam induced damage that causes small structural changes even under very low dose conditions, eventually changing their electrical properties as examined via in situ measurements. In this work, silicon, titanium, and niobium oxide thin films are used for in situ TEM electrical characterization studies. The electron beam induced reduction of the oxides turns these insulators into conductors. The conductivity change is reversible by exposure to air, supporting the idea of electron beam reduction of oxides as primary damage mechanism. Through these measurements we propose a limit for the critical dose to be considered for in situ scanning electron microscopy and TEM characterization studies.

Technetium-99 is considered as one of the most dangerous nuclear environmental pollutants due to its long half-life (210,000 y.) and high mobility in aqueous solutions under oxidizing conditions. Development of sorbents, which are capable of irreversible uptake of Tc and further direct conversion into durable ceramic waste forms, is an important field of research. Titanate ceramic doped with up to 10 wt. % Tc was successfully synthesized using Layered Hydrazinium Titanate, LHT-9 (PCT/EP2010/001864) as starting precursor. LHT-9 is a new advanced compound of general formula (N2H5)1/2Ti1.87O4xH2O containing 6-7 wt. % of hydrazine chemically incorporated into a TiO2-based matrix. It was demonstrated that LHT-9 (5g/l) can reductively adsorb up to 90.2 wt. % of Tc from aqueous solutions containing 0.5g Tc/l. The obtained adsorption products can be easily converted into stable titanate ceramic by one-step sintering in argon atmosphere at 1200°C. Phase and chemical composition of synthesized Tc-doped ceramic are discussed.

Layered hydrazinium titanate LHT-9, (N2H5)1/2Ti1.87O4 is a new nanohybrid material related to lepidocrocite-type titanates. Unique combination of ion exchange, reductive properties, surface activity due to Brønsted acid sites and occurrence of surface titanyl groups allows exploring LHT-9 for simultaneous uptake of almost all components of liquid nuclear wastes. LHT-9 irreversibly removes technetium, molybdenum, palladium and selenium from their aqueous solutions by specific mechanism of reductive adsorption. For removal of cesium, strontium, transition elements, actinides and lanthanides LHT-9 provides mechanisms of ion exchange and surface complexation. Products of adsorption are nanocrystalline and homogeneous powders loaded with 5 to 15 wt. % of radionuclides and non-radioactive elements. LHT-9 can be applied as ready-to-use precursor for one-step synthesis of durable titanate ceramic waste forms similar to SYNROC. An essential advantage of LHT-9 in comparison with other titanate sorbents (monosodium titanate and peroxo-titanate materials) is the absence of Na in its composition that permits arbitrary tailoring of sorbent properties by simple pre-treatment with the desired elements. Results on sorption of americium, cesium, strontium and lanthanides by LHT-9 are discussed.

The high surface to volume ratio of nanoparticles allows a detailed experimental study of the surface phenomena associated with solid bridging. Besides bulk analyses, the local view on the structure and composition via HRTEM is particularly essential. 50 nm core shell particles consisting of a silicon (Si) core and a SiO2 shell were used as model system to understand surface phenomena appearing for Si-based nanostructures. Evaporative drying from de-ionized water shows the most significant bridging effect based on SiO2. There is only a localized deposition of oxides between the particles during the drying process and no overall oxidation. For the deposition material, silicates are the most likely candidates.