Intestinal bacteria are involved in bile acid (BA) deconjugation and/or dehydroxylation and are responsible for the production of secondary BA. However, an increase in the production of secondary BA modulates the intestinal microbiota due to the bactericidal effects and promotes cancer risk in the liver and colon. The ingestion of Bacillus coagulans improves constipation via the activation of bowel movement to promote defaecation in humans, which may alter BA metabolism in the intestinal contents. BA secretion is promoted with high-fat diet consumption, and the ratio of cholic acid (CA):chenodeoxycholic acid in primary BA increases with ageing. The dietary supplementation of CA mimics the BA environment in diet-induced obesity and ageing. We investigated whether B. coagulans lilac-01 and soya pulp influence both BA metabolism and the maintenance of host health in CA-supplemented diet-fed rats. In CA-fed rats, soya pulp significantly increased the production of secondary BA such as deoxycholic acid and ω-muricholic acids, and soya pulp ingestion alleviated problems related to plasma adiponectin and gut permeability in rats fed the CA diet. The combination of B. coagulans and soya pulp successfully suppressed the increased production of secondary BA in CA-fed rats compared with soya pulp itself, without impairing the beneficial effects of soya pulp ingestion. In conclusion, it is possible that a combination of prebiotics and probiotics can be used to avoid an unnecessary increase in the production of secondary BA in the large intestine without impairing the beneficial functions of prebiotics.

The spectro-polarimeter in the Hinode Solar Optical Telescope (SOT) is one of the powerful instruments for the most accurate measurements of vector magnetic fields on the solar surface. The magnetic field configuration and possible candidates for flare trigger are briefly discussed with some SOT observations of solar flare events, which include X5.4/X1.3 flares on 7 March 2012, X1.2 flare on 7 January 2014 and two M-class flares on 2 February 2014. Especially, using an unique set of the Hinode and SDO data for the X5.4/X1.3 flares on 7 March 2012, we briefly reviewed remarkable properties observed in the spatial distribution of the photospheric magnetic flux, chromospheric flare ribbons, and the 3D coronal magnetic field structure inferred by non-linear force-free field modeling with the Hinode photospheric magnetic field data.

A nanoscale dynamic mechanical analysis (nano-DMA) measurement method has been successfully developed for use in evaluating nanoscale dynamic viscoelastic properties in small-scale polymer materials over a range of non-ambient temperatures from -120 oC to 500 oC. Measurements have been obtained with a nanoindentation measurement system, in which two key techniques are applied. One is a thermal protection system for control and prevention of thermal drift and noise. The other is an environmental control system for preventing corrosion at high temperatures and dew condensation at low temperatures. Measurement reliability was examined by using a combination of a thermal-mechanically stable fused silica and a homogeneous sample of isotropic polyethylene terephthalate (PET). Constant hardness and modulus values of the fused silica from -120 oC to 500 oC indicated that the measurements were not affected by thermal load drift and noise even at elevated temperatures. The PET sample exhibited no significant difference in temperature dispersions of storage elastic modulus, loss elastic modulus and loss tangent between the nanoindentation measurement data and bulk data measured with a conventional DMA method. A practical application involving surface-deteriorated polyethylene (PE) tubes was used to demonstrate the validity and usefulness of this nano-DMA method. Infrared spectroscopic imaging revealed that the surface layer of the PE tubes was oxidized to form a carbonylated (O=C<) layer. The storage elastic modulus and glass-transition temperature of the surface layer were much higher than the corresponding values of the interior. These data indicate a plausible reason for why the PE tube surface deteriorates to form brittle cracks.

Nanoscratch test used for small area measurements and four-point bending test applied for quantitative measurements were coupled to evaluate the adhesive strengths of SiCN/Cu/Ta,/TaN/SiO2/Si stacked layers. The similarities and differences of the two methods concerning adhesion, position of the delamination interface, and plastic deformation of the delaminated film were estimated. It was found that the nanoscratch test gave similar adhesion properties when the delamination interface was the same as that formed by the four-point bending test. The four-point bending test displayed clearer results compared to the nanoscratch test because energy for delamination was not used in plastic deformation and the crack could propagate further. These results suggest that coupling the nanoscratch and four-point bending tests is powerful way to estimate and understand adhesion of thin film materials.

A recently developed bidirectional thermal expansion measurement (BTEM) method was applied to different types of low-k films to substantiate the reliability of the Poisson's ratio found with this technique and thereby to corroborate its practical utility. In this work, the Poisson's ratio was determined by obtaining the temperature gradient of the biaxial thermal stress from substrate curvature measurements, the temperature gradient of the whole thermal expansion strain along the film thickness from x-ray reflectivity (XRR) measurements, and reduced modulus of the film from nanoindentation measurements. For silicon oxide-based SiOC film having a thickness of 382.5 nm, the Poisson's ratio, Young's modulus and thermal extension coefficient (TEC) were determined to be Vf = 0.26, αf =21 ppm/K and Ef =9,7 GPa. These data are close to the levels of metals and polymers rather than the levels of fused silicon oxide, which is characterized by Vf = 0.17 and Er = 69.6 GPa. The alkyl component in the silicon oxide-based framework is thought to act as an agent in reducing the modulus and elevating the Poisson's ratio in SiOC low-k materials. In the case of an organic polymer SiLK film with a thickness of 501.5 nm, the Poisson's ratio, Young's modulus and TEC were determined to be Vf = 0.39, αf =74 ppm/K and Er =3.1 GPa, which are in the typical range of V= 0.34~0.47 with E =1.0~10 GPa for polymer materials. From the viewpoint of the relationship between the Poisson's ratio and Young's modulus as classified by different material types, the Poisson's ratios found for the silicon oxide-based SiOC and organic SiLK films are reasonable values, thereby confirming that BTEM is a reliable and effective method for evaluating the Poisson's ratio of thin films.

Over a 25-year period, we encountered 12 patients who died suddenly with coronary arterial lesions due to Kawasaki disease. We report their clinical course, and analyze the happenings of their deaths. Of the 12 patients, 10 were dead on arrival at hospital. Their age at death ranged from 13 months to 27 years, with a median of 16 years, and the interval from the onset of Kawasaki disease to death ranged from 2 months to 24 years. In 4 patients, death was found to be due to myocardial infarction, while in the remaining 8, it could not be determined. In 7 patients, coronary angiograms obtained less than 4 months after the acute onset of Kawasaki disease showed lesions bilaterally, most being giant aneurysms. Myocardial infarction had occurred in 6 patients prior to their death. In 1 patient of the late 1970s, who collapsed after running, cardiac sequels had not been suspected prior to autopsy. During the 1980s, 3 infants with bilateral giant aneurysms died within a year of the initial onset of Kawasaki disease, with acute myocardial infarction being the cause in 2 of them. In the late 1990s, and the 2000s, 5 patients died suddenly with left ventricular dysfunction, their ejection fractions being less than 40 percent more than 20 years after the initial onset of Kawasaki disease. Prior to their sudden deaths, they had had no cardiac events for many years, but had suffered previous myocardial infarctions. Multifocal premature ventricular contractions, and non-sustained ventricular tachycardia, are probable risk factors in such patients. Careful follow-up, checking for ventricular arrhythmia, is needed to prevent sudden death in patients suffering left ventricular dysfunction in the setting of Kawasaki disease.

Background: We have used intravascular ultrasound in an attempt to clarify the extent of vascular remodelling of the aortic arch after the repair of aortic coarctation by use of a subclavian flap. Methods: We investigated 13 patients with coarctation of the aorta, ranging in age from 1.4 to 43.0 months, with a mean of 20.8 months, who underwent aortoplasty by incorporation of a subclavian flap. The mean postoperative period was 19.6 months, with a range from 0.03 to 41.2 months. The luminal morphology of the aortic arch was evaluated by intravascular ultrasound at the time of post-operative catheterization. Results: We observed 3 cases longitudinally. Over the period of observation, we found three types of morphology of the aorta at the site of incorporation of the subclavian flap, namely a snowman shape with two inflection points, a pisiform shape with one inflection point, and a round shape without any points of inflection. There was a correlation between the cross-sectional shapes at the site of the subclavian flap in the postoperative period (p < 0.01). In each case, we measured the cross-sectional area at the site of subclavian flap, at the descending aorta, and at the distal aortic arch. The cross-sectional area, and the increment of the cross-sectional area at the site of subclavian flap, was larger. Conclusion: The shape of the lumen subsequent to repair of aortic coarctation changes progressively from a snowman, to a pisiform, and finally to a round shape. Greater growth of the subclavian flap compared to the native wall of the aorta was observed for at least the first 4 years after repair. This finding may improve our understanding of the remodelling process of the arterial trunks after surgical repair.

A spherical nanoindentation method was developed to evaluate elastic and plastic deformation parameters. The experimental reliability was confirmed by examining fused silica in the elastic deformation range. Yield stress as a quantitative plastic parameter was estimated using the Hertz contact theory and Tresca yield criterion. A copper thin film and two types of low-k thin film were examined. Reduced modulus was almost the same as the value obtained for the Cu (100) plane and yield stress was found to be between single crystals Cu (111) and Cu (100). These mechanical properties were thought to be dependent on the crystal orientation of the copper thin film. The two types of MSQ low-k film exhibited a difference in yield stress, although hardness was estimated to be similar by using the conventional nanoindentation method. These results have never been seen on a micro-mater scale.

A high-temperature nanoindentation measurement method has been developed for evaluating the hardness and modulus of low-k films when the temperature is raised from R.T. to 200°C. Thermal stability and chemical changes due to heating were investigated by Raman spectroscopy, Fourier transform infrared spectroscopy and thermogravimetry-differential thermal analysis, and by thermal desorption spectroscopy, respectively. Two different classes of low-k materials, organic polyarylence ether film and methyl-hydrogen-silsesquioxane film, were examined. The hardness and modulus of the former film during heating increased due to water desorption in the lower temperature range, and then decreased due to the evolution of hydrocarbon gas from some unreacted components or solvent residuals in the higher temperature range. In regard to the latter film, the hardness and modulus of a specimen (A) having a higher hydrocarbon content decreased during heating and reached the lowest value at 200°C and then constantly remained at the lowest levels during cooling. In contrast, no significant changes in hardness and modulus were observed for a specimen (B) having a lower hydrocarbon content in either the heating or cooling process. The reduction of the hardness and modulus of specimen A was attributed to thermal decomposition of most of its Si-CH3 and SiH/SiH2 chains. These results revealed that the temperature dependence of the hardness and modulus of low-k films is significantly affected by physical and/or chemical changes during heating due to moisture absorption, thermal evolution of organic residuals and thermal decomposition, rather than other factors such as thermal stress.

Light-induced degradation of photoconductive properties is investigated as a function of lightinduced Si dangling bond defect concentration and subgap absorption. This relation is studied for a variety of sample preparation techniques including a-Si:D, wide range of temperatures during light exposure and annealing, and sample degradation pre-history. Under a given exposure condition, light-induced defects have a fixed effective electron capture coefficient, while its value varies greatly with exposure conditions (temperature during exposure or stepwise anneal) and with sample microstructure. This explains commonly observed non-linear dependences and hysteresis between defect concentration and mobility-lifetime product. Creation efficiency of less-stable defects with large capture coefficients is not influenced by the presence of a large number of stable defects. Structural change accompanying the defect creation, if any, is strongly related to the defect creation and is likely to occur locally around the defects, modifying their capture coefficients. Capture can vary both because of the changes in intrinsic capture probabilities and due to changes in the net defect charge balance. The former may be increased by the presence of H or photocarrier trap (e.g. weak bond tail state) in a close vicinity of Si dangling bond. The latter may be caused by a wide distribution of defect states in the gap or by simultaneous creation of negatively charged floating bond states near VB edge.

The preparation of amorphous silicon films and solar cells using SiH2Cl2 source gas and electron cyclotron resonance assisted chemical vapor deposition (ECR-CVD) was investigated. By using buffer layers to protect previously deposited layers improved a-Si:H(Cl) solar cells were prepared and studied. The high quality a-Si:H(Cl) films used in this study exhibited low defect densities (~1015cm-3) and high stability under illumination even when the deposition rate was increased to ~15A/s. The solar cells were deposited in the n-i-p sequence. These solar cells achieved VOC values of ~ 0.89V and ~ 3.9% efficiency on Ga doped ZnO (GZO) coated specular substrate. The a-Si:H(C1) electron and hole μτ products were ~10-8cm2/V.

1. We collected 27 pairs of twins (MZ 21, DZ 6) ranging from 41 to 80 years, and 16 pairs of homosexual siblings (SL) ranging from 62 to 90 years, all of whom were Japanese in the western district of Honshū-Island. First, we measured the bodily constitution, certain body parts and certain bones, and investigated their life- histories. Next, we investigated various senescent phenomena. That is: — the approximate number of gray hairs on the head, the appearance and the size of alopecia senilis in the parietal region, the approximate number of wrinkles in the frontal region, the comparative number of sulci cutis on the nape of neck, the back of the right hand, and the anterior chest, the development of senile pigment spots on the face, the back of the right hand, the extensor surface of the right forearm, and the upper half of the back, the appearance of the senile wart, the development of pinguecula, the development of arcus senilis, the development of marginal protuberances on the lumbar vertebral bodies, and the upper end of the tibia, the existence of fabella in the right knee, and the calcification in the wall of the arch of the aorta.

With regard to these items we calculated the middle percentage deviation, the coefficient of correlation, or the rate of concordance, and on the photographs or X-ray photographs the resemblance between both partners was examined.

2. We have concluded that the following items are mainly subject to the control of heredity. That is, the approximate number of gray hairs on the head, the existence, the localization and the shape of alopecia senilis on the parietal region in ♂, the localization and the shape of wrinkles on the frontal region, the localization and the development of senile pigment spots on the face, the development of pinguecula and of arcus senilis of the eye, the development and the shape of marginal protuberances on the lumbar vertebral body, and the development of marginal protuberances on condylus lateralis et medialis of the tibia. On the other hand, the following items were found to be fairly subject to influence of the environmental factors. That is, the appearance of alopecia senilis on the parietal region in ♀, the number of wrinkles on the frontal region, the comparative number of sulci cutis on the nape of neck, the back of the right hand, and the anterior chest, the number of senile pigment spots on the back of the right hand, the extensor surface of the right forearm, and the upper half of the back, the appearance of senile wart on the body, and the calcification in the arch of the aorta.

3. Concerning those senescent phenomena, which are strikingly subject to the control of heredity, a certain degree of difference between both partners of MZ was sometimes recognized. When the differences in the progression of various senescent phenomena between both partners of MZ were observed, it was often recognized that some senescent phenomena make more progress in one partner, while on the other hand the other ones do in another partner.

4. In order to decide certain environmental factors, which have influence upon the difference between both partners of MZ, we referred to the existence of heavy labor for long duration, the number of deliveries, the grade of the sunburn, the habit of alcoholic drinking, smoking, and history of various diseases. However, we could not decide that some of these factors had certain definite relationship with the progression of certain senescent phenomena. However, we might probably presume that the old-styled Japanese hair dressing worn for many years had a certain relationship with the appearance of the baldness in ♀.