Adhesion of a-C:F during oxygen plasma annealing

Published online by Cambridge University Press:  15 February 2011

Y. Matsubara
Affiliation:
ULSI Device Development Labs., 1120, Shimokuzawa, Sagamihara, Kanagawa, 229–11, Japan
K. Endo
Affiliation:
Microelectronics Res. Labs. NEC Corporation 1120, Shimokuzawa, Sagamihara, Kanagawa, 229–11, Japan
T. Tatsumi
Affiliation:
34 Miyukigaoka, Tsukuba, Ibaraki, 305, Japan
T. Horiuchi
Affiliation:
ULSI Device Development Labs., 1120, Shimokuzawa, Sagamihara, Kanagawa, 229–11, Japan
Get access

Abstract

Fluorinated amorphous carbon (a-C:F) films sandwiched between layers of SiO2 have been proposed as an interlayer dielectric (ILD) structure in order to enhance resistance to oxygen plasma. This study describes adhesion failure mechanisms for the sandwiched fluorinated amorphous carbon film (a-C:F) structure during oxygen plasma annealing. We have found 3 failure modes: 1) capping SiO2 layer peels off, 2) thickness reduction of a-C:F by decomposition, and 3) etching phenomena at the interface between SiO2 and a-C:F by CFx outgassing from a-C:F. The outgassed CFx radicals were stored at the interfaces and the etching of SiO2 occurred during the subsequent 150°C oxygen plasma resist removal process. Thermal decomposition of a-C:F ILD sandwiched between layers of SiO2 was performed to determine the outgassed species, as well as the thickness reduction of a-C:F.

Type
Research Article
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Paraszczak, J. et al. , Tech. Digest IEEE IEDM, p.261, (1993).Google Scholar
[2] Endo, K. and Tatsumi, T., J. Appl. Phys. 78, p. 1370, (1995).Google Scholar
[3] Matsubara, Y. et al. , Tech. Digest IEEE IEDM, p.369, (1996).Google Scholar
[4] Uttrcht, R. R. et al. , Proc. of IEEE VMIC, p.20, (1991).Google Scholar
[5] Endo, K. and Tatsumi, T., Appl. Phys. Lett. 68, P. 2864, (1996).Google Scholar
[6] Heller, S. R. and Milne, G. W. A., EPA/NIH Mass Sectral Data Basevol. 1, national Bureau of Standards, 1978.Google Scholar