Cracking During Nanoindentation and its Use in the Measurement of Fracture Toughness

  • D. S. Harding (a1), W. C. Oliver (a2) and G. M. Pharr (a1)


Results of an investigation aimed at developing a technique by which the fracture toughness of a thin film or small volume can be determined in nanoindentation experiments are reported. The method is based on the radial cracking which occurs when brittle materials are deformed by a sharp indenter such as a Vickers or Berkovich diamond. In microindentation experiments, the lengths of radial cracks have been found to correlate reasonably well with fracture toughness, and a simple semi-empirical method has been developed to compute the toughness from the crack lengths. However, a problem is encountered in extending this method into the nanoindentation regime with the standard Berkovich indenter in that there are well defined loads, called cracking thresholds, below which indentation cracking does not occur in most brittle materials. We have recently found that the problems imposed by the cracking threshold can be largely overcome by using an indenter with the geometry of the corner of a cube. For the cube-corner indenter, cracking thresholds in most brittle materials are as small as 1 mN (∼ 0.1 grams). In addition, the simple, well-developed relationship between toughness and crack length used for the Vickers indenter in the microindentation regime can be used for the cube-corner indenter in the nanoindentation regime provided a different empirical constant is used.



Hide All
1. Pharr, G.M. and Oliver, W.C., MRS Bulletin 17, 28 (1992).
2. Oliver, W.C., MRS Bulletin 11, 15 (1986).
3. Doerner, M.F. and Nix, W.D., J. Mater. Res. 1, 601 (1986).
4. Oliver, W.C. and Pharr, G.M., J. Mater. Res. 7, 1564 (1992).
5. Mayo, M.J. and Nix, W.D., Acta Metall. 36, 2183 (1988).
6. Lawn, B.R., Evans, A.G., and Marshall, D.B., J. Am. Ceram. Soc. 63, 574 (1980).
7. Anstis, G.R., Chantikul, P., Lawn, B.R., and Marshall, D.B., J. Am. Ceram Soc. 64, 533 (1981)
8. Lankford, J., and Davidson, D.L., J. Mater. Sci. 14, 1662 (1979).
9. Hirao, K. and Tomozawa, M., J. Am. Ceram. Soc. 70, 497 (1987).
10. Arora, A., Marshall, D.B., Lawn, B.R., and Swain, M.V., J. Non-Cryst. Sol. 31, 415 (1979).
Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

MRS Online Proceedings Library (OPL)
  • ISSN: -
  • EISSN: 1946-4274
  • URL: /core/journals/mrs-online-proceedings-library-archive
Please enter your name
Please enter a valid email address
Who would you like to send this to? *


Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed