The Effect of Fine M2C (M: Mo, Cr, Fe) Particles on the Recrystallization Temperature and High Temperature Strength of Warm Rolled Fe3Al Based Alloys

Published online by Cambridge University Press:  18 January 2011

Satoru Kobayashi
Affiliation:
Osaka Center for Industrial Materials Research, Institute of Materials Research, Tohoku University, 1-1 Gakuen-cho, Naka-ku, Sakai, Osaka 599-8531, Japan
Takayuki Takasugi
Affiliation:
Osaka Center for Industrial Materials Research, Institute of Materials Research, Tohoku University, 1-1 Gakuen-cho, Naka-ku, Sakai, Osaka 599-8531, Japan Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University, 1-1 Gakuen-cho Naka-ku, Sakai, Osaka 599-8531, Japan
Get access

Abstract

The effect of fine M2C particles on the recrystallization temperature and high temperature strength of warm rolled Fe3Al base alloys was investigated. Fe-27Al-1.2C-2Cr-xMo (x: 0.3, 0.9) alloys (in at.%) were arc melted, warm rolled and annealed. TEM observations have revealed that fine M2C particles were present in the alloy containing 0.9% Mo but not in the alloy with 0.3% Mo after warm rolling. The recrystallization temperature increased from 740 °C to 810 °C when the Mo content is increased from 0.3 to 0.9 due to the presence of fine M2C particles. Tensile tests conducted on annealed samples with fine sub-grained matrix have shown that the introduction of fine M2C particles is effective to enhance the proof stress at 600 °C.

Type
Research Article
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Klöwer, J. in Oxidation of Intermetallics edited by Grabke, H.J. et al. , (Wiley-VCH, Weinheim, 1997) p. 203.Google Scholar
2. Sikka, V.K. in Processing, Properties and Applications of Iron Aluminides, edited by Schneibel, J.H. and Crimp, M.A., (TMS, Warrendale, PA, 1994) pp. 318.Google Scholar
3. Stoloff, N.S., Mater. Sci. Eng., A 258, 1 (1998).Google Scholar
4. Kobayashi, S., Zaefferer, S., Mater. Sci. Forum 558-559, 235 (2007).Google Scholar
5. Kobayashi, S., Takasugi, T., Intermetallics 15, 1659 (2007).Google Scholar
6. Kobayashi, S., Zambaldi, C., Raabe, D., Acta Mater. 58, 6672 (2010).Google Scholar
7. Kobayashi, S. et al. , presented at the 5th Discussion Meeting on the Development of Innovative Iron Aluminium Alloys FEAL 2009, Prague, 2009 (unpublished).Google Scholar
8. Humphreys, F.J., Hatherly, M., Recrystallization and related annealing phenomena. 2nd ed. (Elsevier Ltd, Oxford, UK, 2004) p. 207.Google Scholar
9. Kobayashi, S., Zaefferer, S., Raabe, D., Mater. Sci. Forum, 550, 345 (2007).Google Scholar
10. Sikka, V.K. in International Symposium on Nickel and Iron Aluminides, (ASM International, Materials Park, OH, 1997) p. 361.Google Scholar
11. Kratochvíl, P., Karlík, M., Haušild, P., Cieslar, M., Intermetallics 7, 847 (1999).Google Scholar