BaAl2Si2O8 and SrAl2Si2O8 were synthesized by solid-state reaction of stoichiometric mixtures of either BaCO3 or SrCO3 with coal fly ash and Al2O3. The mixtures were mechanically activated in an attrition mill for up to 12 h and then reaction-sintered at 900-1300 °C, aiming to promote the formation of BaAl2Si2O8 and SrAl2Si2O8 as well as the conversion from their hexagonal (Hexacelsian) into their monoclinic (Celsian) forms, which is associated with improved mechanical properties in the sintered materials. Especially in the case of SrAl2Si2O8, the formation of Celsian was favored at relatively low sintering temperatures by increasing milling time. Although only the SrAl2Si2O8 composition was fully converted into Celsian, the Hexacelsian to Celsian conversions obtained for the mechanically-activated BaAl2Si2O8 composition were significantly higher than those previously reported in the literature for this compound. This could be attributed to the use of coal fly ash as raw material, which contains mineralizers that promote the mentioned conversion.
Email your librarian or administrator to recommend adding this journal to your organisation's collection.
Full text views
* Views captured on Cambridge Core between September 2016 - 30th May 2017. This data will be updated every 24 hours.