Experimental Determination of the Ti-Nb-Al Phase Diagram At 1200°C.

Published online by Cambridge University Press:  26 February 2011

T. J. Jewett ,
J. C. Lin ,
N. R. Bonda ,
L. E. Seitzman ,
K. C. Hsieh ,
Y. A. Chang  and
J. H. Perepezko
T. J. Jewett
Affiliation:
University of Wisconsin-Madison, 1509 University Ave., Madison, sWI 53706.
J. C. Lin
Affiliation:
University of Wisconsin-Madison, 1509 University Ave., Madison, sWI 53706.
N. R. Bonda
Affiliation:
University of Wisconsin-Madison, 1509 University Ave., Madison, sWI 53706.
L. E. Seitzman
Affiliation:
University of Wisconsin-Madison, 1509 University Ave., Madison, sWI 53706.
K. C. Hsieh
Affiliation:
University of Wisconsin-Madison, 1509 University Ave., Madison, sWI 53706.
Y. A. Chang
Affiliation:
University of Wisconsin-Madison, 1509 University Ave., Madison, sWI 53706.
J. H. Perepezko
Affiliation:
University of Wisconsin-Madison, 1509 University Ave., Madison, sWI 53706.
Get access

Abstract

Studies consisting of both bulk sample and diffusion couple experiments have been conducted in order to establish an isothermal section of the Ti-Nb-Al system. Bulk samples were prepared by arc-melting and then annealed in a gettered, flowing, argon atmosphere for extended equilibration periods. The results obtained so far have established the existence of two ternary phases with the following approximate compositions, TI (Ti-18 at% Nb-34 at% Al) and T2 (Ti-ll at% Nb-44 at% Al). Moreover, several of the binary phases were found to have extensive solubilities, including the TiAl phase. The phases TiAl3 and NbAl3 form a continuous solid solution. Several heterogeneous equilibria were also determined. Determination of these phase fields was accomplished through the use of electron microprobe analysis (EMPA), x-ray diffraction, microstructural observations and backscatter electron imaging (BEI).

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 133: Symposium H – High-Temperature Ordered Intermetallic Alloys III , 1988 , 69
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Sridharan, S. and Nowotny, H., Z. Metallkde., 7 468 (1983).Google Scholar
2. Hanamura, T., Uemori, R. and Tanino, M., J. Mater. Res. 3 656 (1988).CrossRefGoogle Scholar
3. Popov, I. A. and Rabezova, V. I., Russ. J. Inorg. Chem., 7 222 (1962).Google Scholar
4. Popov, I. A. and Rabezova, V. I., “Titan i ego Splavy, Akad. Nauk. SSSR. Institut. Metallurg. Z 105 (1962).Google Scholar
5. Banerjee, D., Gogia, A. K., Nandi, T. K. and Joshi, V. A., Acta. Metall. in print.Google Scholar
6. Strychor, R. and Williams, J. C., in Solid-State Phase Transfoformations, TMS-AIME, New York, 249 (1980).Google Scholar
7. Prinzbach, F. and Winter, H., in The Science, technology and Application of Titanium, (Eds: Jaffee, R. I. and Promisel, N. E.), Pergamon Press, London, 875 (1970).Google Scholar
8. Sastry, S. M. L. and Lipsitt, H. A., “Proc. Forth Int. Conf. on Ti.” (Eds: Kimura, H. and Izumi, O.) TMS-AIME, Warrendale, PA,2 123 (1980).Google Scholar