Fracture Strengths of Individual Grain Boundaries in Ni3Ai Using a Miniaturized Disk Bend Test

Published online by Cambridge University Press:  25 February 2011

Douglas E. Meyers  and
Alan J. Ardell
Douglas E. Meyers
Affiliation:
Department of Materials Science and Engineering, University of California, Los Angeles. CA 90024–1595
Alan J. Ardell
Affiliation:
Department of Materials Science and Engineering, University of California, Los Angeles. CA 90024–1595
Get access

Abstract

The results of our initial efforts at measuring the fracture strengths of grain boundaries In Ni3Al using a miniaturized disk-bend test are presented. The samples tested were 3 mm in diameter and between 150 and 300 μm thick. An Ingot of directlonally-solidlfled, boron-free Ni3Al containing 24% Al was annealed between 1300 and 1350 °C to induce grain growth, producing many grain boundaries In excess of 1.5 mm in length. Specimens were cut from these In such a way that one long grain boundary was located near a diameter of the specimen. The relative orientations of the grains on either side of the boundary were determined from electron channeling patterns. Low-angle boundaries are so strong they do not fracture; Instead the samples deform In a completely ductile manner. High-angle boundaries always fracture, but only after considerable plastic deformation of the two grains flanking them. Fracture is Indicated by a load drop in the load vs. displacement curves. A method involving extrapolation of the elastic portion of these curves to the displacement at fracture is used to estimate the fracture stresses. This procedure yields consistent values of the fracture strengths of high-angle boundaries. The measured stresses are large (∼2 to 3 GPa), but considerably smaller than those required for the fracture of special boundaries, as predicted by computer simulations. No correlation was found between the fracture stresses or loads and the geometry of the high-angle boundaries, many of which are close to, but deviate from, coincident site lattice orientations.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 238: Symposium Cb – Structure and Properties of Interfaces in Materials , 1991 , 375
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Aokl, K. and Izuml, O., J. Jpn Inst. Metals 43, 1190 (1979).Google Scholar
2. Uu, C. T., White, C. L. and Horton, J. A., Acta Met. 33, 213 (1985).Google Scholar
3. Schulson, E. M., Weihs, T. P., Baker, I., Frost, H. J. and Horton, J. A., Acta Met. 24, 1395 (1986).Google Scholar
4. Chen, S. P.. Voter, A. F. and Srolovltz, D. J.. Scripta Met. 20, 1389 (1986).Google Scholar
5. Chen, S. P., Voter, A. F., Albers, R. C., Boring, A. M. and Hay, P. J., J. Mater. Res. 5. 955 (1990).Google Scholar
6. Hanada, S., Ogura, T., Watanabe, S., Izuml, O. and Masumoto, T.. Acta Met. 34, 13 (1986).Google Scholar
7. Lin, H. and Pope, D. P., in Alloy Phase Stability and Design, edited by Stocks, G. M.. Pope, D. P. and Glamel, A. S. (Mat. Res. Soc. Symp. Proc. 186, Pittsburgh, PA 1990) p. 329.Google Scholar
8. Mills, M. J., Goods, S. H.. Folles, S. M. and Whetstone, J. R.. Scripta Met. et Mater. 25, 1283 (1991).Google Scholar
9. Li, H., Chen, F. C. and Ardell, A. J., Met. Trans. 22A 2061 (1991).Google Scholar
10. Li, H. and Ardell, A. J.. in High Temperature Ordered Intermetalltc Allovs IV. edited by Johnson, L. A., Pope, D. P. and Stiegler, J. O. (Mat. Res. Soc. Symp. Proc. 213, Pittsburgh, PA 1991) p. 757.Google Scholar
11. F. C Chen. Ardell, A. J. and Pedraza, D. F.. in High Temperature Ordered Intermetalltc Allovs IV. edited by Johnson, L. A., Pope, D. P. and Stiegler, J. O. (Mat. Res. Soc. Symp. Proc. 213, Pittsburgh, PA 1991) P. 763.Google Scholar
12. Zhang, J. and Ardell, A. J.. J. Mater. Res. 6, 1950 (1991).Google Scholar
13. Meyers, D. E., Zhang, J., Chen, F. C. and Ardell, A. J.. (unpublished research. 1991)Google Scholar
14. Goux, C., Mem. Sci. Rev. Metall. 58, 661 (1961).Google Scholar
15. Mykura, H.. in Grain Boundary Structure and Kinetics, edited by Balluffi, R. W. (ASM Mater. Sci. Semin. Milwaukee, WI. 1979). p. 445.Google Scholar
16. Kokawa, H., Watanabe, T. and Karashima, S.. Phil. Mag. 44, 1239 (1981).Google Scholar
17. Pumphrey, P. H., In Grain Boundary Structure and Properties edited by Chadwick, G. A. and Smith, D. A. (Academic Press, London, 1976), p. 139.Google Scholar
18. Roarke, R. J. and Young, W. C., Formulas for Stress and Strain. 5th edit., McGraw Hill Book Company. New York (1975). p. 382.Google Scholar
19. Giovan, M. N. and Sines, G.. J. Amer. Ceram. Soc. 62, 510 (1979).Google Scholar