Friction and Wear Behavior of a Cobalt-Based Alloy Implanted with Ti or N

Published online by Cambridge University Press:  25 February 2011

S. A. Dillich ,
R. N. Bolster  and
I. L. Singer
S. A. Dillich
Affiliation:
Code 6170, Chemistry Division, Naval Research Laboratory, Washington, D.C. 20375;
R. N. Bolster
Affiliation:
Code 6170, Chemistry Division, Naval Research Laboratory, Washington, D.C. 20375;
I. L. Singer
Affiliation:
Code 6170, Chemistry Division, Naval Research Laboratory, Washington, D.C. 20375;
Get access

Abstract

Dry sliding friction tests and relative abrasive wear measurements were used to investigate the effects of ion implantation on the tribology of a centrifugally cast Co-Cr-W-C alloy. Titanium implantation was found to significantly reduce the friction and wear of the alloy. Auger spectroscopy showed that vacuum carburization of the surface occurred during Ti implantation. Similar Ti and C profiles were seen in both carbide and (Co-rich) matrix phases. The abrasive wear resistance of the alloy decreased as a result of N-implantation. Nitrogen implantation did not reduce the friction during dry sliding, however, a change in the wear mode was observed.

Information

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 27: Symposium E – Ion Implantation and Ion Beam Processing of Materials , 1983 , 637
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1. Antony, K.C., J. of Metals, Feb. 1973, 52–60.Google Scholar
2. Bhansali, K. J. and Miller, A.E., Wear, 75 (1982) 241–252.Google Scholar
3. Blomberry, R.I. and Perrot, C.M., J. Aust. Inst. Met. V19 #4 (1974) 254–258.Google Scholar
4. Heathcock, C.J.. Ball, A. and Protheroe, B.E., Wear 74 (1981–1982) 1126.Google Scholar
5. Hartley, N.E.W., in Treatise on Materials Science and Technology, V18 Ion Implantation, ed. Hirvonen, J.K. (Academic Press, N.Y. 1980) 321–368.Google Scholar
6. Dearnaley, G., Radiation Effects (1982) V63, 1–15.Google Scholar
7. Singer, I.L., Carosella, C.A. and Reed, J.R., Nucl. Inst. and Meth. 182/183 (1981) 923–932.Google Scholar
8. Singer, I.L., Bolster, R.N. and Carosella, C.A., Thin Solid Films, 73 (1980) 283–289.Google Scholar
9. Singer, I.L. and Jeffries, R.A., J. Vac. Sci. and Technol. A1 (1983) 317–321.Google Scholar
10. Dillich, S.A. and Singer, I.L., Thin Solid Films, 108 No. 2, 1983, 219–227.Google Scholar
11. Bolster, R.N. and Singer, I.L., Appl. Phys. Lett. 36 (1979) 208–209.Google Scholar
12. Singer, I.L., J. Vac. Sci. Technol. A1 (1983) 419–422.Google Scholar
13. Dillich, S.A., Sprague, J.A. and Singer, I.L., to be published.Google Scholar
14. Oliver, W.C. et al. , these proceedings.Google Scholar
15. Vardiman, R.G., Bolster, R.N. and Singer, I.L., in Metastable Materials Formation by Ion Implantation, Picraux, S.T. and Choyke, W.J., ed. (Elsevier Science Publ. Co. Inc., 1982) 269–273.Google Scholar
16. Cobalt Monagraph, Centre D'Information Du Cobalt, Brussels, (1960) 167.Google Scholar