Immobilisation of Simulated Plutonium-Contaminated Material in Phosphate Glass: An Initial Scoping Study

  • Paul A. Bingham (a1), Russell J. Hand (a1) and Charlie R. Scales (a2)

Vitrification is a potential route for the immobilisation of Plutonium Contaminated Material (PCM). This is an Intermediate Level Waste (ILW) arising from operations in which there is contact with Pu isotopes. PCM consists of low levels of Pu combined with metals, masonry, glass, ceramics, polymers and other carbonaceous materials. Simulated PCM containing CeO2 as a PuO2 surrogate was mixed with a phosphate precursor and vitrified. Pre-oxidation of PCM simulant prior to vitrification minimised the violence of batch reactions. No pre-oxidation produced inhomogeneous slag-like materials with high residual metals and particulates. Pre-oxidation at 600°C in air and at 1200°C in an O2-rich atmosphere produced more favourable results, with increasingly vitreous products resulting from more oxidised PCM simulant. The most oxidised PCM simulant produced phosphate glasses with low levels of particulate inclusions, as confirmed by x-ray diffraction and scanning electron microscopy. Particulates included iron-rich metallics and aluminous oxides. Increased melting times and temperatures may have reduced the number of inclusions slightly, but O2 bubbling during melting resulted in little additional benefit. Waste loading equivalent to ∼60 weight % of untreated waste may be possible. There was little evidence of Ce partitioning, indicating that it was immobilised within the glass matrix and had little preference for metallic or crystalline phases. These results demonstrate the potential feasibility for vitrification of PCM in phosphate glass, justifying further investigation into this potentially novel solution.

Hide All
1. Management of plutonium contaminated waste, Ed. Grover J. R., Harwood Academic Publishers, London, 1981.
2. Donald I. W., Metcalfe B. L. and Taylor N. J., J. Mat. Sci. 32, 5851 (1997).
3. Hyatt N. C., personal communication.
4. Bingham P. A. and Hand R. J., J. Hazard. Mater., B119, 125 (2005).
5. Bingham P. A., Hand R. J., Forder S. D. and Lavaysierre A., J. Hazard. Mater., B122, 129 (2005).
6. Mesko M. G. and Day D. E., J. Nucl. Mater., 273, 27 (1999).
7. Kim D. S., Vienna J. D., Hrma P. and Cassingham N., Ceram. Trans., 143, 337 (2003).
8. Rabiger W., Keldenich K. and Scheffler J., Glastech. Ber. Glass Sci. Technol. 68, 85 (1995).
9. Colombo P., Brusatin G., Bernardo E. and Scarinci G., Curr. Opin. Solid State Mat. Sci., 7, 225 (2003).
10. Tzeng C. C., Kuo Y. Y., Huang T. F., Lin D. L. and Yu Y. J., J. Hazard. Mater., 58, 207 (1998).
11. Darab J. G., Li H., Schweiger M. J., Vienna J. D., Allen P. G., Bucher J. J., Edlestein N. M., Shuh D. K., Proc. Plutonium Futures '97, New Mexico, 143 (1997).
12. Ramsey W. G., Bibler N. E., Meaker T. F., WSRC-MS-94-0550;
Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

MRS Online Proceedings Library (OPL)
  • ISSN: -
  • EISSN: 1946-4274
  • URL: /core/journals/mrs-online-proceedings-library-archive
Please enter your name
Please enter a valid email address
Who would you like to send this to? *


Full text views

Total number of HTML views: 0
Total number of PDF views: 3 *
Loading metrics...

Abstract views

Total abstract views: 22 *
Loading metrics...

* Views captured on Cambridge Core between September 2016 - 13th December 2017. This data will be updated every 24 hours.