Infiltration of Al-Mg Alloy into SiC Preform in the Production of Metal Matrix Composites by Pressureless Infiltration

Published online by Cambridge University Press:  14 March 2011

A. Zulfia  and
R.J. Hand
A. Zulfia
Affiliation:
Department of Metallurgy, The University of Indonesia, Kampus Baru UI, Depok 16424, Indonesia Department of Engineering Materials, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield, S1 3JD, UK
R.J. Hand
Affiliation:
Department of Metallurgy, The University of Indonesia, Kampus Baru UI, Depok 16424, Indonesia Department of Engineering Materials, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield, S1 3JD, UK
Get access

Abstract

Molten Al-Mg alloys has been infiltrated into SiC to produce Al matrix composites at 900oC for different infiltration times under N2. The wettability of the ceramic reinforcement by the Al-Mg alloy is crucial in determining whether Al can be infiltrated into ceramic preform. Sessile drop results showed that Al alloys with Mg contents greater than 8wt-% had a contact angle lower than 90o, after 5 minutes contact time, this was associated with the infiltration of Al-Mg alloys into SiC preform occurred after 30 minutes. Sessile drop experiments also show that SiC is similarly wetted by Al-Mg alloys under N2. It is concluded that the infiltration process does not involve the intermediate nitride phase suggested by other authors. These materials were also charaterised both mechanical properties and microstructure.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 702: Symposium U – Advanced Fibers, Plastics, Laminates and Composites , 2001 , U8.6.1
Copyright
Copyright © Materials Research Society 2002

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Ray, S., J Mater Sci, 28, (1993), 5397–5413 Google Scholar
2. Martin, G.P., Olsen, D.L. and Edwards, G.R., Met Trans 19B (1988) 95 Google Scholar
3. Aghajanian, M.K., Burke, J.T., White, D.R. and Nagelberg, A.S., SAMPE Q, 20, (1989) 43 Google Scholar
4. Aghajanian, M.K., Rocazella, M.A., Burke, J.T. and Keck, S.D., J Mater Sci, 26 (1991) 447 Google Scholar
5. Mortensen, A. and Cornie, J.A., Metal Trans. A, 18, (1987), 1160–1163 Google Scholar
6. Clyne, T.W. and Bader, M.G., Fifth International Conference on Composites Materials: ICCM.V. San Diego, CA, (1985), 755–771 Google Scholar
7. Yang, X.F. and Xi, X.M., J Mater Sci, 30, (1995), 5099–5102 Google Scholar
8. McCoy, J.W., Jones, C. and Warner, F.E., SAMPE Q, 19 (2), (1988), 37 Google Scholar
9. Schiroky, G.H., Miller, D.V., Aghajanian, M.K., and Fareed, A.S., Key Engineering Materials, Vols. 127–131, (1997), 141–152 Google Scholar
10. Watari, T., K.Mori, Torikai, T. and Matsuda, O., J. Am, Ceram, Soc, 77(10), 1997, 2599–2602 Google Scholar
11. Llyod, D.J., Lagace, H., McLeod, A., and Morris, P.L., Mater Sci Eng, Vol A107, (1989), 73 Google Scholar
12. Llyod, D.J. and Jin, I., Metal Trans A, Vol 19A,(1988), 3107–3109 Google Scholar
13. Viala, J.C., Fortier, P., and Bouix, J., J. Mater Sci, Vol. 25(3), (1990), 1842–1850 Google Scholar
14. Chen, Y.Y. and Chung, D.D.L., J Mat Sci, 31 (1986) 407–412 Google Scholar
15. Choh, T., Kobashi, M., Nakata, H., and Kaneda, H., Mat Sci Forum Vol. 217–222, (1996) 353–358 Google Scholar
16. Lee, K.B. and Kwon, H., Scripta Materialia, Vol. 36, No.8, (1997), 847–852 Google Scholar
17. McEvoy, A.J., Williams, R.H., and Higginbotham, I.G., J. Mater Sci, 11, (1976), 297 Google Scholar
18. Bardal, A., Mater Sci & Eng, A159, (1992), 119–125 Google Scholar
19. Papworth, A. and Fox, P., Mater Sci Tech, 13, (1997), 912–917 Google Scholar
20. Gu, X. and Hand, R.J., J. European Ceramic Society, 16, (1996), 929–935 Google Scholar
21. Zulfia, A. and Hand, R.J., Materials Science and Technology, Vol. 16, (2000), 867–872 Google Scholar
22. Warren, R. and Andersson, C.H., Composites, Vol. 15, (1984), 101–111 Google Scholar
23. Iseki, T., Kameda, T., and Maruyama, T., J. Mater Sci, Vol. 19, (1984), 1692–1698 Google Scholar
24. Lloyd, D.J., Composites Science and Technology, 35, (1989), 159–179 Google Scholar
25. Lee, K.B., Kim, Y.S., and Kwon, H., Metal Trans A, 29, (1998), 3087–3095 Google Scholar