Microstructure of Ultra High Dose Self Implanted Silicon

Published online by Cambridge University Press:  10 February 2011

X. F. Zhu ,
J. S. Williams ,
D. J. Llewellyn  and
J. C. McCallum
X. F. Zhu
Affiliation:
Department of Electronic Materials Engineering, Research School of Physical Sciences and Engineering, Australian National University, Canberra, ACT 0200, Australia
J. S. Williams
Affiliation:
Department of Electronic Materials Engineering, Research School of Physical Sciences and Engineering, Australian National University, Canberra, ACT 0200, Australia
D. J. Llewellyn
Affiliation:
Department of Electronic Materials Engineering, Research School of Physical Sciences and Engineering, Australian National University, Canberra, ACT 0200, Australia
J. C. McCallum
Affiliation:
School of Physics, University of Melbourne, Parkville, 3052, Australia
Get access

Abstract

This study has investigated the microstructure of ultra high dose (∼ 1018 cm−2) self implantation into Si. Implants have been carried out into both (100) Si and pre-amorphised Si as a function of implant temperature between liquid nitrogen temperature and 350°C. Results show that high dose implantation into completely amorphous Si (a-Si) produces layers which regrow quite well during subsequent solid phase epitaxy. In contrast, implantation into crystalline Si (c-Si) or part amorphous/part crystalline Si can lead to rich and varied microstructures at elevated temperatures, even extending to porous-like structures in some cases. Strong dynamic annealing and agglomeration of points defects in c-Si is thought to be responsible for such behaviour.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 504: Symposium KK – Atomistic Mechanisms in Beam Synthesis & Irradiation… , 1997 , 27
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Olson, G.L. and Roth, J.A., Mat.Sci. Reports 3 (1988) 1.Google Scholar
2. Appleton, B.R., Holland, O.W., Narayan, J., Schow, O.E. III, Williams, J.S., Short, K.T. and Lawson, E.M., Appl.Phys.Lett. 41 (1982) 711.Google Scholar
3. Huber, H. et.al. Nucl.Instrum.Meth. (in press 1997).Google Scholar
4. Eaglesham, D.J. et.al, in Microscopy of Semiconducting Materials, Oxford, 1995, ed. Cullis, A.G. and Stanton-Bevan, A.E. [Inst. Phys. Conf. Ser. 146, 451 (1995)].Google Scholar
5. Holland, O.W., Xie, L., Nielson, B. and Zhou, D.S., J.Elec.Mat. 25 (1996) 99.Google Scholar
6. Wong-Leung, J., Nygren, E. and Williams, J.S., Appl.Phys.Lett. 68 (1995) 417.Google Scholar
7. Myers, S.M., Follstaedt, D. and Bishop, D.M., Mat.Res.Soc.Symp.Proc. 316 (1994) 33.Google Scholar
8. Hu, J.Z., Merkle, L.D., Menoni, C.S. and Spain, I.L., Phys.Rev. B34 (1986) 4679.Google Scholar
9. Williams, J.S. et.al. Mat.Res.Soc.Symp.Proc. 27 (1984) 205.Google Scholar
10. Zhu, X.F. and Williams, J.S., to be published.Google Scholar
11. Williamson, D.L., Rooda, S., Chicoine, M., Tabti, R., Stolk, P.A., Acco, S. and Saris, F.W., Appl.Phys.Lett. 67 (1995) 226.Google Scholar
12. Rooda, S., Cliche, L., Chicoine, M. and Masut, R.A., Nucl.Instrum.Meth. B106 (1995) 80.Google Scholar
13. Williams, J.S., Trans.Mat.Res.Soc.Jpn. 17 (1994) 417.Google Scholar