Preparation, Structure and Mechanical Properties of RuAl and (Ru,Ni)Al Alloys

Published online by Cambridge University Press:  15 February 2011

A. L. R. Sabariz  and
G. Taylor
A. L. R. Sabariz
Affiliation:
Department of Materials, University of Oxford, Oxford OX1 3PH, U.K.
G. Taylor
Affiliation:
Department of Materials, University of Oxford, Oxford OX1 3PH, U.K.
Get access

Abstract

The intermetallic compound, RuAl with B2 CsCl type structure, has been shown to possess room-temperature toughness and plasticity. NiAl also forms a B2 compound and it is claimed that a pseudo-binary compound, (Ru,Ni)Al, may be formed because the difference in lattice parameter between the two binary phases is slight. In this work a study has been made of the mechanical properties of some polycrystalline compounds, across the RuAl-(Ru,Ni)Al pseudo-binary, prepared from high-purity elemental powders. Compressive yield stresses were measured between room-temperature and 900°C, and the mechanisms of plastic flow are discussed in relation to the dislocation structures observed by TEM. Hot-microhardness tests were made to provide an indication of the effect of solid-solution hardening.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 460: Symposium Z – High-Temperature Ordered Intermetallic Alloys VII , 1996 , 611
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Fleischer, R.L., J. Mat. Sci., 22, 2281 (1987).Google Scholar
2. Fleischer, R.L., Briant, C.L. and Field, R.D. in High-Temperature. Ordered Intermetallic alloys IV. edited by Johnson, L.A., Pope, D.P. and Stiegler, J.O. (Mat. Res. Soc. Proc. 213, Pittsburgh, Pa 1991) p. 463.Google Scholar
3. Fleischer, R.L., Field, R.D. and Briant, C.L., Metallurgical Transactions A, 22A, 403 (1991).Google Scholar
4. Chakravorty, S. and West, D.R.F., Scripta Metallurgica, 19, 1355 (1985).Google Scholar
5. Chakravorty, S. and West, D.R.F., Journal of Material Science, 21, 2721 (1986).Google Scholar
6. Wolffand, I.M. Sauthoff, G., Metallurgical and Materials Transactions A, 27A, 1395 (1996).Google Scholar
7. Wolffand, I.M. Sauthoff, G., Metallurgical and Materials Transactions A, 27A, 2642 (1996).Google Scholar
8. Yi, H.C. and Moore, J.J., J. Mat. Sci., 25, 1159 (1990).Google Scholar
9. Cullity, B.D., Elements of X-rav Diffraction. 2nd Ed (Addison - Weley, Reading, Ma, 1978) p. 363.Google Scholar
10. German, R.M., Particle Packing Characteristics (Metal Powder Industries Federation, NJ, 1989) p. 160 Google Scholar
11. Wu, Y.P., Sanchez, J.M. and Tien, J.K. in High Temperature Ordered Intermetallic Alloys III, edited by Liu, C.T., Taub, A.I., Stoloff, N.S. and Koch, C.C. (Mat. Res. Soc. Proc. 133, Pittsburgh, PA, 1989) 119 Google Scholar
12. Rudy, M. anf Sauthoff, G., Mater. Sei. Eng., 81, 525 (1986).Google Scholar
13. Yoo, M.H., Takasugi, T., Hanada, S. and Izumi, O., Trans. JIM, 31, 435 (1990).Google Scholar
14. Lin, W., Liu, J.H. and Freeman, A.J., J. Mater. Res., 7, 592 (1992).Google Scholar