Process Monitoring for a-Si:H Materials and Interfaces

Published online by Cambridge University Press:  26 February 2011

R. W. Collins  and
J. M. Cavese
R. W. Collins
Affiliation:
BP America Research and Development. 4440 Warrensville Center Road, Cleveland, OH 44128
J. M. Cavese
Affiliation:
BP America Research and Development. 4440 Warrensville Center Road, Cleveland, OH 44128
Get access

Abstract

Real time ellipsometry results are presented which have been useful in characterizing nucleation, interface formation, and surface modification for hydrogenated amorphous silicon (a-Si:H) thin films and device structures. Earlier studies of the effect of deposition procedure on a-Si:H nucleation are reviewed, and new data on plasma-enhanced CVD p-type a-Si:H are discussed. Changes in the initial microstructural coalescence are observed when gas phase concentrations of 0.2% B2H6 are added to SiH4 to obtain the p-type films. When depositing p-type a-Si:H on undoped a-Si:H at 180°C and 250°C. ellipsometry allows detection of film formation at the rate of a few monolayers/minute by CVD (in the absence of plasma excitation) from the doping gas mixture. CVD requires both SiH4 and B2H6 in the gas. Other interesting aspects of this process are presented. Finally, in situ ellipsometry is applied with H2 plasmas and ion beams to study near-surface Si-Si bond breaking and etching. A common effect of many of these treatments is a reduction in the density of Si-Si bonds in the film bulk by 6–8%.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 118: Symposium E – Amorphous Silicon Technology , 1988 , 19
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Hottier, F. and Theeten, J.B., J. Cryst. Growth 48, 644 (1980).CrossRefGoogle Scholar
[2] Drevillon, B., Thin Solid Films 130, 165 (1985).Google Scholar
[3] Collins, R.W. and Cavese, J.M., J. Appl. Phys. 61, 1869 (1987).Google Scholar
[4] Collins, R.W. and Cavese, J.M., J. Appl. Phys. 61, 1662 (1987).Google Scholar
[5] Collins, R.W. and Tuckerman, C.J., J. Vac. Sci. Technol. 4, 2343 (1986).Google Scholar
[6] Collins, R.W., Tuckerman, C.J., Huang, C.-Y., and Windischmann, H., J. Vac. Sci. and Technol. A 3, 2077 (1985).Google Scholar
[7] Aspnes, D.E., Thin Solid Films 89, 249 (1982).CrossRefGoogle Scholar
[8] Bruggeman, D.A.G., Ann. Phys. (Leipzig) 24, 636 (1935).CrossRefGoogle Scholar
[9] Aspnes, D.E., Theeten, J.B., and Hottier, F., Phys. Rev. B 20, 3292 (1979).Google Scholar
[10] Stutzmann, M., Biegelsen, D.K., and Street, R.A., Phys. Rev. B 35, 5666 (1987).Google Scholar
[11] Street, R.A., Mat. Res. Soc. Symp. Proc. 95, 13 (1987).Google Scholar
[12] Collins, R.W., Soc. Photo-Opt. Instrum. Eng. 617, 62 (1986).Google Scholar
[13] Aspnes, D.E. and Studna, A.A., AppI. Opt. 14, 220 (1975).Google Scholar
[14] Aspnes, D.E., Soc. Photo-Opt. Instrum. Eng. 276, 188 (1981).Google Scholar
[15] McMarr, P.J., Vedam, K. and Narayan, J., J. Appl. Phys. 59, 694 (1986).CrossRefGoogle Scholar
[16] Collins, R.W. and Cavese, J.M., J. Non-Cryst. Solids 97&98, 269 (1987).Google Scholar
[17] Neugebauer, C.A. in Handbook of Thin Film Technology, edited by Maissel, L.I. and Glang, R. (McGraw-Hill, New York, 1970), Chapt. 8, p. 7–9.Google Scholar
[18] Antoine, A.M., Drevillon, B., and Cabarrocas, P. R. i, J. Appl. Phys. 61, 2501 (1987).Google Scholar
[19] Gallagher, A., Mater. Res. Soc. Symp. Proc. 70, 3 (1986).CrossRefGoogle Scholar
[20] Tsai, C.C., Knights, J.C. Chang, G., and Wacker, B., J. Appl. Phys. 59, 2998 (1986).Google Scholar
[21] Tanaka, K., and Matsuda, A., Mater. Sci. Rep. 2. 139 (1987).Google Scholar
[22] Drevillon, B., Perrin, J., Siefert, J.M., Huc, J., Lloret, A., de Rosny, G., and Schmitt, J.P.M., Appl. Phys. Lett. 42, 801 (1983).Google Scholar
[23] The reference dielectric function was obtained by correcting the pseudo-dielectric function for surface roughness deduced from in situ data.Google Scholar
[24] Schiff, E.A., Persans, P.D., Fritzsche, H., and Akopyan, V.. Appl. Phys. Lett. 38, 92 (1981).CrossRefGoogle Scholar
[25] Hirose, M., J. Phys. (Paris) 42, C4–705 (1981).Google Scholar
[26] Farrow, R.F.C. and Filby, J.D., J. Electrochem. Soc. 118, 149 (1971).Google Scholar
[27] Collins, R.W. and Cavese, J.M., J. Vac. Sci. Technol. A 5, 2797 (1987).Google Scholar
[28] Aspnes, D.E., Studna, A.A., and Kinsbron, E., Phys. Rev. B 29, 768 (1984). Our reference data for a-Si:H are consistent with a 0.02 lower Si-Si bond volume fraction in comparison to the low pressure CVD material in this study.CrossRefGoogle Scholar