Residual Stresses and Resulting Damage Within Fibers Intersecting A Free Surface

Published online by Cambridge University Press:  15 February 2011

J. M. Galbraith ,
M. N. Kallas ,
D. A. Koss  and
J. R. Hellmann
J. M. Galbraith
Affiliation:
Center for Advanced Materials, The Pennsylvania State University, University Park, PA 16802
M. N. Kallas
Affiliation:
Center for Advanced Materials, The Pennsylvania State University, University Park, PA 16802
D. A. Koss
Affiliation:
Center for Advanced Materials, The Pennsylvania State University, University Park, PA 16802
J. R. Hellmann
Affiliation:
Center for Advanced Materials, The Pennsylvania State University, University Park, PA 16802
Get access

Abstract

Finite element as well as indentation fracture mechanics modeling have been used to analyze the evolution of fiber damage that was observed at the ends of fibers intersecting a free surface in sapphire-reinforced TiAl matrix composites. Experimental observations indicate that, under certain conditions, surface cracks introduced during cutting will propagate along the fiber axis due to thermally-induced residual stresses. Finite element computations predict that significant thermally-induced residual tensile stresses exist near the ends of sapphire fibers which are embedded within TiAl-based matrices and are oriented normal to a free surface. Crack growth behavior induced by microhardness indentations is used to experimentally verify the FEM predictions. The results indicate that a biaxial tensile residual stress state exists near the fiber ends due to a thermal expansion mismatch. The magnitude of the residual stresses are a sensitive function of interfacial bond strength and elastic/plastic properties of the interfacial region and may be sufficient to propagate pre-existing cracks.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 273: Symposium Q – Intermetallic Matrix Composites II , 1992 , 119
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Lawn, B. R. and Fuller, E. R. Jr., J. Mater. Sci. 19, 4061–4067 (1984).CrossRefGoogle Scholar
2. Marshall, D. B. and Lawn, B. R., J. Am. Ceram. Soc. 60 (1–2), 86–87 (1977).Google Scholar
3. Tandon, R. and Green, D. J., J. Am. Ceram. Soc. 73 (4), 970–977 (1990).Google Scholar
4. Gruninger, M. F., Lawn, B. R., Farabaugh, E. N., and Wachtman, J. B. Jr., J. Am. Ceram. Soc. 70 (5), 344–348 (1987).Google Scholar
5. Lawn, B. R., in Fracture Mechanics of Ceramics. Vol. 5, edited by Bradt, R. C., Evans, A. G., Hasselman, D. P. H., and Lange, F. F. (Plenum Press, New York, 1983) pp. 1–25; H. P. Kirchner and E. D. Isaacson, Fracture Mechanics of Ceramics. (Plenum Press, New York, 1983), pp. 57–70.Google Scholar
6. Lawn, B. R. and Wilshaw, T. R., J. Mater. Sci. 10, 1049 (1975).Google Scholar
7. Lawn, B. R. and Swain, M. V., J. Mater. Sci. 10, 113 (1975).Google Scholar
8. Marshall, D. B. and Lawn, B. R., J. Mater. Sci. 14, 2001–2012 (1979).Google Scholar
9. Lawn, B. R., Marshall, D. B., and Evans, A. G., J. Am. Ceram. Soc. 63, 574–581 (1980).Google Scholar
10. Tada, H., Paris, P. C., and Irwin, G. R., The Stress Analysis of Cracks Handbook (Dell Research Corp., Hellertown, PA, 1973), p. 24.2.Google Scholar
11. Kallas, M. N., Koss, D. A., Hahn, H. T., and Hellmann, J. R., J. Mater. Sci. 22 (to be published in 1992).Google Scholar
12. Iwasa, M. and Bradt, R. C., Bull. Am. Ceram. Soc. 60, 374 (1981).Google Scholar