Rutherford Backscattering Spectrometry Studies on Copper and Chromium Diffusion in Polyimide

Published online by Cambridge University Press:  22 February 2011

Kyung W. Paik  and
Arthur L. Ruoff
Kyung W. Paik
Affiliation:
Department of Materials Science and Engineering, Cornell University, Ithaca, NY 14853
Arthur L. Ruoff
Affiliation:
Department of Materials Science and Engineering, Cornell University, Ithaca, NY 14853
Get access

Abstract

Diffusion of Cu in polyimide(PI) film was observed after Cu evaporation on PI at room temperature. Annealing treatment significantly enhanced the diffusion of Cu. The diffusion coefficient measured at 200 and 400 C using the Fickian erfc solution are 3 × 10−14 and 1 × 10−13 cm2/sec, respectively. Cu shows the Fickian diffusion behavior. In contrast to Cu, no clearly measurable diffusion had occurred for an as-deposited Cr specimen and a specimen annealed at 400 C for 1 hour. However, for longer annealing times a slight amount of Cr diffused into PI because of the growth of the intermixed region. The diffusion coefficients of Cr at 200 and 400 C for less than 20 hours are 2 × 10−15 and 7 × 10−15 cm2/sec, respectively. The diffusion of Cr in PI shows non-Fickian behavior.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 153: Symposium J – Interfaces Between Polymers, Metals, and Ceramics , 1989 , 143
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Chou, N.J. and Tang, C.H., J. Vac. Sci. Technol., A2(2), 751 (1984)Google Scholar
2. Tromp, R.M., Legoues, F., and Ho, P.S., J. Vac. Sci. Technol., A3(3) 782, (1985)Google Scholar
3. LeGoues, F.K., Silverman, B.D. and Ho, P.S., J. Vac. Sci. Technol., A6(4), 2200 (1988)Google Scholar
4. Ohuchi, F.S. and Freilich, S.C., J. Vac. Sci. Technol., A4(3), 1039 (1986)Google Scholar
5. Chu, W.-K., Mayer, J.W. and Nicolet, M.-A., Backscattering Spectrometry, Academic, New York (1978)Google Scholar
6. Doolittle, L., Nucl. Instrum. & Methods, B9, 344 (1985)Google Scholar
7. Romanelli, J.F., Mayer, J.W., Kramer, E.J., J. Polym. Sci. Polym. Phys. Ed., 24, 263 (1986)Google Scholar
8. Chou, N.J., Dong, D.W., Kim, J., and Liu, A.C., J. Electrochem. Soc., 131(10), 2335 (1984)Google Scholar
9. Goldberg, M.J., Clabes, J.G., and Kovac, C.A., J. Vac. Sci. Technol., A6(3) 991 (1988)Google Scholar
10. Haight, R., White, R.C., Silverman, B.D., and Ho, P.S., J. Vac. Sci. Technol., A6(4), 2188 (1988)Google Scholar