In situ stress analysis of multilayer environmental barrier coatings

  • B. J. Harder (a1), J. Almer (a2), K. N. Lee (a3) and K. T. Faber (a1)
Abstract

The biaxial stress and thermal expansion of multilayer doped-aluminosilicate environmental barrier coatings were measured in situ during cooling using microfocused high-energy X-rays in transmission. Coating stresses during cooling from 1000 °C were measured for as-sprayed and thermally cycled samples. In the as-sprayed state, tensile stresses as high as 75 MPa were measured in the doped-aluminosilicate topcoat at 375 °C, after which a drop in the stress occurred accompanied by through-thickness cracking of the two outermost layers. After thermally cycling the samples, the stress in the topcoat was reduced to approximately 50 MPa, and there was no drop in stress upon cooling. This stress reduction was attributed to a crystallographic phase transformation of the topcoat and the accompanying change in thermal expansion coefficient. The addition of a doped aluminosilicate to the mullite layer did not lower the stress in the topcoat, but may offer increased durability due to an increased compressive stress.

Copyright
Linked references
Hide All

This list contains references from the content that can be linked to their source. For a full set of references and notes please see the PDF or HTML where available.

J. Almer , U. Lienert , R. L. Peng , C. Schlauer , and M. Oden (2003). “Strain and texture analysis of coatings using high-energy x-rays,” J. Appl. Phys.JAPIAU0021-897994, 697702.10.1063/1.1582351

A. G. Evans and J. W. Hutchinson (1984). “On the mechanics of delamination and spalling in compressed films,” Int. J. Solids Struct.IJSOAD0020-768320, 455466.10.1016/0020-7683(84)90012-X

K. T. Faber , C. M. Weyant , B. H. Harder , J. Almer , and K. N. Lee (2007). “Internal stresses and phase stability in multiphase environmental barrier coatings,” Int. J. Mater. Res.IJMRFV1862-528298, 1188–95.

M. J. Hyatt and N. P. J. Bansal (1996). “Crystal growth kinetics in BaOAl2O32SiO2 and SrOAl2O32SiO2 glasses,” Mater. Sci.MSCJDS0137-133931, 172184.10.1007/BF00355142

N. S. Jacobson (1993). “Corrosion of silicon-based ceramics in combustion environments,” J. Am. Ceram. Soc.JACTAW0002-782076, 328.10.1111/j.1151-2916.1993.tb03684.x

J. B. Kimmel , N. Miriyala , J. R. Price , K. L. More , P. F. Tortorelli , H. E. Eaton , G. D. Linsey , and E. Y. Sun (2002). “Evaluation of CFCC liners with EBC after field testing in a gas turbine,” J. Eur. Ceram. Soc.JECSER0955-221922, 27692775.10.1016/S0955-2219(02)00142-5

K. N. Lee , D. S. Fox , J. I. Eldridge , D. M. Zhu , R. C. Robinson , N. P. Bansal , and R. A. Miller (2003). “Upper temperature limit of environmental barrier coatings based on mullite and BSAS,” J. Am. Ceram. Soc.JACTAW0002-782086, 12991306.

K. N. Lee (2000b). “Key durability issues with mullite-based environmental barrier coatings for Si-based ceramics,” J. Eng. Gas Turbines PowerJETPEZ0742-4795122, 632636.10.1115/1.1287584

K. N. Lee , R. A. Miller , and N. S. Jacobson (1995). “New generation of plasma-sprayed mullite coatings on silicon carbide,” J. Am. Ceram. Soc.JACTAW0002-782078, 705710.10.1111/j.1151-2916.1995.tb08236.x

I. C. Noyan and J. B. Cohen (1987). Residual Stress: Measurement by Diffraction and Interpretation (Springer-Verlag, New York).

E. J. Opila (1999). “Variation of the oxidation rate of silicon carbide with water-vapor pressure,” J. Am. Ceram. Soc.JACTAW0002-782082, 18261834.10.1111/j.1151-2916.1999.tb02005.x

J. L. Smialek , R. C. Robinson , E. J. Opila , D. S. Fox , and N. S. Jacobson (1999). “SiC and Si3N4 recession due to SiO2 scale volatility under combustor conditions,” Adv. Compos. Lett.ZZZZZZ0963-69358, 3345.10.1163/156855199X00056

M. D. Thouless (1991). “Cracking and delamination of coatings,” J. Vac. Sci. Technol. AJVTAD60734-21019, 25102515.10.1116/1.577265

Y. S. Touloukian , R. K. Kirby , R. E. Taylor , and T. Y. Lee (1977). Thermal Expansion of Nonmetallic Solids (Plenum, New York), Vol. 13.

C. M. Weyant , K. T. Faber , J. D. Almer , and J. V. Guiheen (2005). “Residual stress and microstructural evolution in tantalum oxide coatings on silicon nitride,” J. Am. Ceram. Soc.JACTAW0002-782088, 21692176.

C. M. Weyant , K. T. Faber , J. D. Almer , and J. V. Guiheen (2006). “Residual stress and microstructural evolution in environmental barrier coatings of tantalum oxide alloyed with aluminum oxide and lanthanum oxide,” J. Am. Ceram. Soc.JACTAW0002-782089, 971978.10.1111/j.1551-2916.2005.00830.x

Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Powder Diffraction
  • ISSN: 0885-7156
  • EISSN: 1945-7413
  • URL: /core/journals/powder-diffraction
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords:

Metrics

Full text views

Total number of HTML views: 2
Total number of PDF views: 4 *
Loading metrics...

Abstract views

Total abstract views: 122 *
Loading metrics...

* Views captured on Cambridge Core between September 2016 - 28th July 2017. This data will be updated every 24 hours.