Refinement of the Structure of MnSi by Powder Diffraction

Published online by Cambridge University Press:  10 January 2013

Jens-Erik Jørgensen  and
Svend Erik Rasmussen
Jens-Erik Jørgensen
Affiliation:
Department of Inorganic Chemistry, Aarhus University DK-8000 Aarhus C, Denmark
Svend Erik Rasmussen
Affiliation:
Department of Inorganic Chemistry, Aarhus University DK-8000 Aarhus C, Denmark
Get access Rights & Permissions [Opens in a new window]

Abstract

Crystal data and results of structure refinements for MnSi are reported. The material is cubic, P213, with a = 4.5603(2) Å, Vd = 94.84(1) Å3, Z = 4, Dx = 5.815 Mg/m3. Intensity data were obtained from a Stoe transmission type diffractometer equipped with a position sensitive detector. CuKα1 radiation, λ = 1.5405981 Å was employed. Germanium was used as an internal standard for the determination of the lattice constant (aGe= 5.6582 Å). The structure was refined by the Rietveld method by aid of three different programs.

Information

Type
Research Article
Information
Powder Diffraction , Volume 6 , Issue 4 , December 1991 , pp. 194 - 195
Copyright
Copyright © Cambridge University Press 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

Bérar, J.-F. & Lenann, P. (1991). J. Appl. Cryslallogr. 24, 1.Google Scholar
Borén, B. (1933). Arkiv för Kemi, Mineralogi och Geologi, Bd 11 A, N:o 10, 1.Google Scholar
Hansen, A. (1958). Constitution of Binary Alloys, McGraw-Hill Book Company.CrossRefGoogle Scholar
Guinier, A. (1963). X-Ray Diffraction, W. H. Freeman and Company, p. 104.Google Scholar
Hill, R.J. & Madsen, I. C. (1987). Powder Diffraction 2, 146.Google Scholar
Phragmén, G. (1923). Jernkontorets Annaler 107, 131Google Scholar
Larson, A. C. & Von Dreele, R. B. (1987). Report No. IA-UR-86-748. Los Alamos Laboratory, Los Alamos, USA.Google Scholar
Morrey, J. R. (1968). Anal. Chem. 40, 905.Google Scholar
Rietveld, H. M. (1969). J. Appl. Crystallogr. 2, 65.CrossRefGoogle Scholar
Smith, G. S. & Snyder, R. L. (1979). J. Appl. Cryslallogr. 12, 60–65.Google Scholar
Wiles, D. B. & Young, R. A. (1981). J. Appl. Crystallogr. 14, 149.Google Scholar