Fracture modes in micropillar compression of brittle crystals

  • Philip R. Howie (a1), Sandra Korte (a1) and William J. Clegg (a1)
Abstract
Abstract

This article describes cracking during microcompression of Si, InAs, MgO, and MgAl2O4 crystals and compares this with previous observations on Si and GaAs micropillars. The most common mode of cracking was through-thickness axial splitting, the crack growing downward from intersecting slip bands in pillars above a critical size. The splitting behavior observed in all of these materials was quantitatively consistent with a previous analysis, despite the differences in properties and slip geometry between the different materials. Cracking above the slip bands also occurred either in the side or in the top surface of some pillars. The driving forces for these modes of cracking are described and compared with observations. However, only through-thickness axial splitting was observed to give complete failure of the pillar; it is, therefore, considered to be the most important in determining the brittle-to-ductile transitions that have been observed.

Copyright
Corresponding author
a)Address all correspondence to this author. e-mail: prh33@cam.ac.uk
Linked references
Hide All

This list contains references from the content that can be linked to their source. For a full set of references and notes please see the PDF or HTML where available.

1.M.D. Uchic , D.M. Dimiduk , J.N. Florando , and W.D. Nix : Sample dimensions influence strength and crystal plasticity. Science 305, 986 (2004).

2.J.R. Greer and W.D. Nix : Size dependence of mechanical properties of gold at the sub-micron scale. Appl. Phys. A 80, 1625 (2005).

3.H. Bei , S. Shim , E.P. George , M. Miller , E. Herbert , and G. Pharr : Compressive strengths of molybdenum alloy micro-pillars prepared using a new technique. Scr. Mater. 57, 397 (2007).

4.F. Östlund , P.R. Howie , R. Ghisleni , S. Korte , K. Leifer , W.J. Clegg , and J. Michler : Ductile-brittle transition in micropillar compression of GaAs at room temperature. Philos. Mag. 91, 1190 (2011).

5.F. Östlund , K. Rzepiejewska-Malyska , K. Leifer , L.M. Hale , Y. Tang , R. Ballarini , W.W. Gerberich , and J. Michler : Brittle-to-ductile transition in uniaxial compression of silicon pillars at room temperature. Adv. Funct. Mater. 19, 2439 (2009).

6.J. Michler , K. Wasmer , S. Meier , F. Östlund , and K. Leifer : Plastic deformation of gallium arsenide micropillars under uniaxial compression at room temperature. Appl. Phys. Lett. 90, 043123 (2007).

7.S. Korte and W.J. Clegg : Discussion of the dependence of the effect of size on the yield stress in hard materials studied by microcompression of MgO. Philos. Mag. 91, 1150 (2010).

8.S.J. Lloyd , J.M. Molina-Aldareguia , and W.J. Clegg : Deformation under nanoindents in sapphire, spinel and magnesia examined using transmission electron microscopy. Philos. Mag. A. 82, 1963 (2002).

9.A. Kelly , G.W. Groves , and P. Kidd : Crystallography and Crystal Defects (Wiley, Chichester, 2000).

10.S. Bouvier and A. Needleman : Effect of the number and orientation of active slip systems on plane strain single crystal indentation. Modell. Simul. Mater. Sci. Eng. 14, 1105 (2006).

11.J.J. Gilman : Chemistry and Physics of Mechanical Hardness (Wiley, New York, 2009).

12.S. Korte and W. Clegg : Micropillar compression of ceramics at elevated temperatures. Scr. Mater. 60, 807 (2009).

14.J. Deneen Nowak , W.M. Mook , A.M. Minor , W.W. Gerberich , and C.B. Carter : Fracturing a nanoparticle. Philos. Mag. 87, 29 (2007).

15.J. Deneen , W.M. Mook , A.M. Minor , W.W. Gerberich , and C.B. Carter : In situ deformation of silicon nanospheres. J. Mater. Sci. 41, 4477 (2006).

16.W.W. Gerberich , W.M. Mook , C.R. Perrey , C.B. Carter , M.I. Baskes , R. Mukherjee , A. Gidwani , J. Heberlein , P.H. McMurry , and S.L. Girshick : Superhard silicon nanospheres. J. Mech. Phys. Solids. 51, 979 (2003).

17.A.A. Griffith : The phenomena of rupture and flow in solids. Philos. Trans. R. Soc. A. 221, 163 (1921).

18.C. Gurney and J. Hunt : Quasi-static crack propagation. Proc. Roy. Soc. A. 299, 508 (1967).

19.K. Kendall : Complexities of compression failure. Proc. Roy. Soc. A. 361, 245 (1978).

20.K.E. Puttick : The mechanics of indentation fracture in poly (methyl methacrylate). J. Phys. D. 11, 595 (1978).

21.A.R. Beaber , J.D. Nowak , O. Ugurlu , W.M. Mook , S.L. Girshick , R. Ballarini , and W.W. Gerberich : Smaller is tougher. Philos. Mag. 91, 1179 (2011).

23.H. Huang and W.W. Gerberich : Crack-tip dislocation emission arrangements for equilibrium–II. Comparisons to analytical and computer simulation models. Acta Metall. Mater. 40, 2873 (1992).

26.M.F. Ashby and C.G. Sammis : The damage mechanics of brittle solids in compression. Pure Appl. Geophys. 133, 489 (1990).

29.S. Adachi : Physical Properties of III-V Semiconductor Compounds (Wiley-VCH, New York, 1992).

30.F. Ericson and J-Å. Schweitz : Micromechanical fracture strength of silicon. J. Appl. Phys. 68, 5840 (2009).

31.J.J. Wortman and R.A. Evans : Young’s modulus, shear modulus, and Poisson’s ratio in silicon and germanium. J. Appl. Phys. 36, 153 (1965).

32.R.W. Rice , C.C. Wu , and K.R. McKinney : Fracture and fracture toughness of stoichiometric MgAl2O4 crystals at room temperature. J. Mater. Sci. 31, 1353 (1996).

33.A.K. Kushwaha : Vibrational and elastic properties of aluminate spinel MgAl2O4. Physica B 405, 2795 (2010).

34.C.L. Conner and K.T. Faber : Segregant-enhanced fracture in magnesium oxide. J. Mater. Sci. 25, 2737 (1990).

35.D-H. Chung : Elastic moduli of single crystal and polycrystalline MgO. Philos. Mag. 8, 833 (1963).

36.K. Hjort , J. Soderkvist , and J-Å. Schweitz : Gallium arsenide as a mechanical material. J. Micromech. Microeng. 4, 1 (1994).

37.J.L. Beuth : Cracking of thin bonded films in residual tension. Int. J. Solids Struct. 29, 1657 (1992).

38.T. Çağin , J. Che , M.N. Gardos , A. Fijany , and W.A. Goddard : Simulation and experiments on friction and wear of diamond: A material for MEMS and NEMS application. Nanotechnology 10, 278 (1999).

39.F.P. Bowden and C.A. Brookes : Frictional anisotropy in nonmetallic crystals. Proc. Roy. Soc. A 295, 244 (1966).

Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Journal of Materials Research
  • ISSN: 0884-2914
  • EISSN: 2044-5326
  • URL: /core/journals/journal-of-materials-research
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords: