Effects of low-energy electron bombardment on the surface chemical structure and adhesive properties of polytetrafluoroethylene (PTFE)

Published online by Cambridge University Press:  31 January 2011

J.A. Kelber ,
J.W. Rogers Jr.  and
S.J. Ward
J.A. Kelber
Affiliation:
Sandia National Laboratories, Albuquerque, New Mexico 87185
J.W. Rogers Jr.
Affiliation:
Sandia National Laboratories, Albuquerque, New Mexico 87185
S.J. Ward
Affiliation:
Sandia National Laboratories, Albuquerque, New Mexico 87185
Get access

Abstract

The x-ray photoemission studies of polytetrafluoroethylene (PTFE) bombarded by lowenergy electrons in ultra-high vacuum conditions indicate that the major chemical changes induced by electron bombardment are defluorination of the surface and cross-linking of the polymer chains. The same electron bombardment process, when performed in the presence of 1×10−6 Torr ND3, also results in the adsorption of nitrogen-containing groups at the surface. The rate of nitrogen adsorption is linear for short electron bombardment times while the rates of defluorination and cross-linking are roughly exponential. However, at long bombardment times, the rates of nitrogen uptake, defluorination, and cross-linking become zero at the same time, indicating that defluorination of the surface is the rate-determining step in electron beam-induced adsorption of nitrogen-containing species. Regardless of whether the bombardment is carried out in ultra-high vacuum or in the presence of ND3, the maximum modification depth is less than 30 Å. Pull tests performed on PTFE samples bombarded by electrons in ultra-high vacuum, then removed into air and bonded to epoxy show epoxy-PTFE joint strengths of 280–360 1b/in.2 (psi), are compared to zero psi for untreated PTFE and ≃2000 psi for cohesive failure within the PTFE layer.

Type
Articles
Information
Journal of Materials Research , Volume 1 , Issue 5 , October 1986 , pp. 717 - 723
Copyright
Copyright © Materials Research Society 1986

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Clark, D. T. and Feast, W. J., J. Macromol. Sci. Rev. Macromol. Chem. C12, 191 (1975).Google Scholar
2Clark, D. T., Dilks, A., and Shuttleworth, D. in Polymer Surfaces, edited by Clark, D. T. and Feast, W. J. (Wiley, New York, 1978), pp. 185–211, 309-351.Google Scholar
3Wheeler, D. R. and Pepper, S. V., J. Vac. Sci. Technol. 20, 226 (1982).Google Scholar
4Pepper, S. V., J. Appl. Phys. 45, 2947 (1974).Google Scholar
5Wheeler, D. R. and Pepper, S. V., NASA Technical Memorandum No. 83413, 1983.Google Scholar
6Allan, A. J. G., J. Polymer Sci. 24, 461 (1957).CrossRefGoogle Scholar
7The exact values of mean free paths in organic materials for electrons of these energies are the subject of some controversy. A generally accepted value for the C(1s) photoelectron mean free path now seems to be ~30 Å rather than the earlier reported value of 10 Å (Ref. 1), and the 30 Å value is used in this work. See, for example,Google Scholar
Brundle, C. R., Hopster, H., and Swalen, J. D., J. Chem. Phys. 70, 5190 (1979).CrossRefGoogle Scholar
8Collins, G. C. S., Lowe, A. C., and Nicholas, D., Eur. Polymer J. 9, 1173 (1973).Google Scholar
9See, for example, Neave, J. H. and Joyce, B. A., J. Phys. D 10, 243 (1977).Google Scholar
10Evans, J. F. and Kuwana, T., Anal. Chem. 51, 358 (1979).Google Scholar
11Hollohan, J. R., Stafford, B. B., Falb, R. D., and Payne, S. T., J. Appl. Polym. Sci. 13, 807 (1969)Google Scholar
Allred, R. E., Merrill, E. W., and Roylance, D. K. in Molecular Characterization of Polymer Interfaces, edited by Ishidaand, H.Kumar, G. (Plenum, New York, 1985), pp. 333–372.Google Scholar
12Willis, R. F. and Skinner, D. K., Solid State Commun. 13, 685 (1973).CrossRefGoogle Scholar
13Handbook of X-Ray Photoelectron Spectroscopy, edited by Wagner, C. D., Riggs, W. M., Davis, L. E., Moulder, J. F., and Muilenberg, G. E. (Perkin-Elmer Corporation Physical Electronics Division, Eden Prairie, MN, 1979), p. 13.Google Scholar
14McDaniel, E. W., Collision Phenomena in Ionized Gases (Wiley, New York, 1964).Google Scholar
15Menzel, D. and Gomer, R., J. Chem. Phys. 41, 3311 (1964).Google Scholar
16Nishijima, M. and Propst, F., Phys. Rev. B 2, 2368 (1970).Google Scholar
17Chapiro, A., Radiation Chemistry of Polymer Systems (Wiley Interscience, New York, 1962), pp. 526–533.Google Scholar
18Kelber, J. A. and Knotek, M. L., J. Vac. Sci. Technol. A 1, 1149 (1983).Google Scholar
19Seah, M., Surf. Interface Anal. 2, 222 (1980).Google Scholar
20Scofield, J. H., J. Electron Spectrosc. Relat. Phenom. 8, 129 (1976).Google Scholar
21Laborie, P., Rocard, J.-M., and Rees, J. A., Electronic Cross-Sections and Macroscopic Coefficients (Dunod, Paris, 1971), Vol. II.Google Scholar