Fabrication of TiO2 nanospheres by template replication in porous carbon networks

Published online by Cambridge University Press:  06 January 2012

J. C. Kim ,
Y. N. Kim ,
E. O. Chi ,
N. H. Hur ,
S. B. Yoon  and
J-S. Yu
J. C. Kim
Affiliation:
Center for CMR Materials, Korea Research Institute of Standards and Science, Yusong, P.O. Box 102, Daejon 305–600, Korea
Y. N. Kim
Affiliation:
Center for CMR Materials, Korea Research Institute of Standards and Science, Yusong, P.O. Box 102, Daejon 305–600, Korea
E. O. Chi
Affiliation:
Center for CMR Materials, Korea Research Institute of Standards and Science, Yusong, P.O. Box 102, Daejon 305–600, Korea
N. H. Hur
Affiliation:
Center for CMR Materials, Korea Research Institute of Standards and Science, Yusong, P.O. Box 102, Daejon 305–600, Korea
S. B. Yoon
Affiliation:
Department of Chemistry, Hannam University, Daejon 306–701, Korea
J-S. Yu
Affiliation:
Department of Chemistry, Hannam University, Daejon 306–701, Korea
Get access

Abstract

A silica-colloidal template approach was used to prepare monodisperse nanospheres of TiO2. Close-packed arrays of silica spheres were infiltrated with a sucrose precursor used as a source of carbon. The infiltrated sucrose was carbonized by calcination at 800 °C in flowing argon. After removal of the silica spheres by washing with HF, a porous carbon replica remained. The resulting pores in the replica were then filled with a chloroform solution of titanium alkoxide. Nanospheres of TiO2 approximately 200 nm in diameter were obtained after calcination of the organic component at 600 °C in an argon atmosphere and subsequent sintering in air at 700 °C.

Information

Type
Articles
Information
Journal of Materials Research , Volume 18 , Issue 4 , April 2003 , pp. 780 - 783
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

Barbe, C.J., Arendse, F., Comte, P., Jirousek, M., Lenzmann, F., Shkiover, V., and Gratzel, M., J. Am. Ceram. Soc. 80, 3157 (1997).Google Scholar
Oregan, B., Schwartz, D.T., Zakeeruddin, S.M., and Gratzel, M., Adv. Mater. 12, 1263 (2000).3.0.CO;2-T>CrossRefGoogle Scholar
Gopidas, K.R., Bohorques, M., and Kamat, P.V., J. Phys. Chem. 84, 6435 (1999).Google Scholar
Wijnhoven, J.E.G.J. and Vos, W.L., Science 281, 802 (1998).Google Scholar
Rengarajan, R., Jiang, P., Colvin, V., and Mittleman, D., Appl. Phys. Lett. 77, 3517 (2000).Google Scholar
Rubio, J., Oteo, J.L., Villegas, M., and Duran, P., J. Mater. Sci. 32, 643 (1997).CrossRefGoogle Scholar
Kumazawa, H., Otsuki, H., and Sada, E., J. Mater. Sci. Lett. 12, 839 (1993).CrossRefGoogle Scholar
Wei, Y., Wu, R., and Zhang, Y., Mater. Lett. 41, 101 (1999).Google Scholar
Jiang, P., Bertone, J.F., and Colvin, V.L., Science 291, 453 (2001).CrossRefGoogle Scholar
Velev, O.D. and Kaler, E.W., Adv. Mater. 7, 12 (2000).Google Scholar
Stober, W., Fink, A., and Bohn, E., J. Colloid Interface Sci. 26, 62 (1968).CrossRefGoogle Scholar
Yu, J-S., Yoon, S.B., and Chai, G.S., Carbon 39, 1421 (2001).CrossRefGoogle Scholar
Denkov, N.D., Velev, O.D., Kratchevsky, P.A., Ivanov, I.B., Yoshimura, H., and Nagayama, K., Nature 361, 26 (1993).CrossRefGoogle Scholar
Denkov, N.D., Yoshimura, H., and Nagayama, K., Ultramicroscopy 147 (1996).Google Scholar
Horn, M., Schwerdtfeger, C.F., and Meagher, E.P., J. Am. Ceram. Soc. 53, 124 (1970).Google Scholar