Preparation and characterization of Ni(OH)2 nanoparticles coated with dialkyldithiophosphate

Published online by Cambridge University Press:  31 January 2011

Junyan Zhang ,
Shengrong Yang  and
Qunji Xue
Junyan Zhang
Affiliation:
Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Science, Lanzhou 730000, People's Republic of China
Shengrong Yang
Affiliation:
Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Science, Lanzhou 730000, People's Republic of China
Qunji Xue
Affiliation:
Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Science, Lanzhou 730000, People's Republic of China
Get access

Abstract

Ni(OH)2 nanoparticles modified with di-n-hexadecyldithiophosphate (DDP) were prepared by a chemical surface modification method. The structure of the nanocluster was investigated using infrared spectroscopy, x-ray photoelectron spectroscopy, x-ray diffraction, transmission electron microscopy, and 31P nuclear magnetic resonance spectroscopy. The thermal stability of DDP coating on the Ni(OH)2 nanoparticles was compared to that of pyridinium di-n-hexadecyldithiophosphate (PyDDP) using thermogravimetric analysis. It was found that coated Ni(OH)2 nanoparticles had an average diameter of about 5 nm. Surface modification with DDP prevented water adsorption and effectively improved the dispersive capacity and antioxidative stability of Ni(OH)2 nanoparticles. The thermal stability of DDP coatings on the surface of nano-Ni(OH)2 particles was higher than that of PyDDP coatings because of the chemical interaction between PyDDP and Ni(OH)2 during the coating process.

Type
Articles
Information
Journal of Materials Research , Volume 15 , Issue 2 , February 2000 , pp. 541 - 545
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Chakravorty, D. and Giri, A.K., Chemistry for the 21st Century: Chemistry of Advanced Materials, edited by Rao, C.N.R (Oxford Blackwell Scientific, London, United Kindgom, 1993).Google Scholar
2.Henglein, A., Chem. Rev. 89, 1861 (1989).CrossRefGoogle Scholar
3.Zhou, H.S., Honma, L., Komiyama, H., and Haus, J.W., J. Phys. Chem. 97, 895 (1993).CrossRefGoogle Scholar
4.Kormann, C., Bahnemann, D.W., and Hoffmann, M.R., J. Phys. Chem. 92, 5196 (1988).CrossRefGoogle Scholar
5.Wang, Y. and Herron, H., J. Phys. Chem. 95, 525 (1991).CrossRefGoogle Scholar
6.Gaynor, A.G., Gonzalez, R.J., Davis, R.M., and Zallen, R., J. Mater. Res. 12, 1755 (1997).CrossRefGoogle Scholar
7.Vemury, S., Pratsinis, S.E., and Kibbey, L., J. Mater. Res. 12, 1031 (1997).CrossRefGoogle Scholar
8.Steigerwald, M.L., Alivisatos, A.P., and Brus, L.E., J. Am. Chem. Soc. 110, 3046 (1988).CrossRefGoogle Scholar
9.Steigerwald, M.L. and Brus, L.E., Acc. Chem. Res. 23, 183 (1990).CrossRefGoogle Scholar
10.Jahanmir, S., Abrahamson, E.P., and Suh, N.P., Wear 40, 75 (1976).CrossRefGoogle Scholar
11.Gawne, D.T. and Ma, U., Wear 129, 123 (1989).CrossRefGoogle Scholar
12.Chen, L.G., Dong, J.X., and Chen, G.X., Trib. Trans. 40, 339 (1997).CrossRefGoogle Scholar
13.Zhang, J.Y., Liu, W.M., Xue, Q.J., and Wang, Q.H., Wear 216, 35 (1998).CrossRefGoogle Scholar
14.Trindade, T., Brien, P.O., and Zhang, X., Chem. Mater. 9, 523 (1997).CrossRefGoogle Scholar
15.Zhang, Z.J., Zhang, J., and Xue, , J. Phys. Chem. 98, 12973 (1994).CrossRefGoogle Scholar
16.Xu, T., Zhang, Z.J., Zhao, J.Z., and Xue, Q.J., Mater. Res. Bull. 31, 345 (1996).CrossRefGoogle Scholar
17.Xue, Q.J., Liu, W.M., and Zhang, Z.J., Wear 213, 29 (1997).CrossRefGoogle Scholar
18.Waters, D.N. and Paddy, J.L., Spectrochim. Acta 44A, 393 (1988).CrossRefGoogle Scholar
19.Matijevic, E. and Scheiner, P., J. Colloid Interface Sci. 63, 509 (1978).CrossRefGoogle Scholar
20.Matijevic, E., Ann. Rev. Mater. Sci. 15, 483 (1985).CrossRefGoogle Scholar
21.Matijevic, E., Pure Appl. Chem. 60, 1479 (1988).CrossRefGoogle Scholar
22.Matijevic, E. and Wan, Peter Hu, J. Colloid Interface Sci. 118, 506 (1987).CrossRefGoogle Scholar
23.Mcivor, R.A., Grant, G.A., and Hubley, C.E., Can. J. Chem. 34, 1611 (1956).CrossRefGoogle Scholar
24.Marion, L., Ramsay, D.A., and Jones, R.N., J. Am. Chem. Soc 73, 305 (1951).CrossRefGoogle Scholar
25.Nakamoto, K., Infrared Spectra of Inorganic and Coordination Compounds (John Wiley, New York, 1963).Google Scholar
26.Lucchesi, P.J. and Glassen, W.A., J. Am. Chem. Soc. 78, 1347 (1956).CrossRefGoogle Scholar
27.Kober, F.P., J. Electrochem. Soc. 112, 1064 (1965).CrossRefGoogle Scholar
28.Moulder, J.F., Stickle, W.F., Sobol, P.E., and Bomber, K.D., Handbook of X-ray Photoelectron Spectroscopy (Physical Electronics, Inc., 1995).Google Scholar
29.Mani, B. and de Neufville, J.P., J. Electrochem. Soc. 135, 800 (1988).CrossRefGoogle Scholar