Reciprocating wear mechanisms in a Zr-based bulk metallic glass

  • H.W. Jin (a1), R. Ayer (a1), J.Y. Koo (a1), R. Raghavan (a2) and U. Ramamurty (a2)...
Abstract

The dry sliding friction coefficient μ and the wear volume loss W, in a zirconium-based bulk metallic glass (BMG) under high-frequency (50 Hz) reciprocating conditions, were investigated with the objective of assessing the influence of free volume and crystallization on the wear behavior of amorphous metals. The BMG samples were annealed either below the glass transition temperature Tg to induce structural relaxation and hence reduce the free volume that controls plasticity through shear-band formation or above Tg to crystallize the amorphous BMG prior to wear testing. Results show that the wear behavior of both the as-cast and relaxed glasses was dominated by the oxidation of the surface layers. A sharp transition in the contact electrical resistance complemented by a marked increase in μ was noted. This was attributed to the formation of a thick tribo film with high oxygen concentration and its subsequent delamination. The μ values, before as well as after the transition, in the relaxed glasses were similar to those for the as-cast alloy. However, a gradual decrease in W with annealing temperature was observed. A good correlation between W and nanohardness was noted, implying that the intrinsic hardness in the BMGs controlled the wear rate.

Copyright
Corresponding author
a) Address all correspondence to this author. e-mail: ramu@materials.iisc.ernet.in
References
Hide All
1Klement W., Willens R.H., and Duwez P.: Noncrystalline structure in solidified gold-silicon alloys. Nature 187, 869 (1960).
2Inoue A.: Bulk amorphous and nanocrystalline alloys with high functional properties. Mater. Sci. Eng., A 304–306, 1 (2001).
3Schneider S.: Bulk metallic glasses. J. Phys.: Condens. Matter 13, 7723 (2001).
4Wang W.H., Dong C., and Shek C.H.: Bulk metallic glasses. Mater. Sci. Eng., R 44, 45 (2004).
5Spaepen F.: A microscopic mechanism for steady state in homogeneous flow in metallic glasses. Acta Metall. 25, 407 (1977).
6Anis M., Rainforth W.M., and Davies H.A.: Wear behavior of rapidly solidified Fe68Cr18Mo2B12. Wear 172, 135 (1994).
7Gloriant T.: Microhardness and abrasive wear resistance of metallic glasses and nanostructured composite materials. J. Non-Cryst. Solids 316, 96 (2003).
8Li G., Wang Y.Q., Wang L.M., Gao Y.P., Zhang R.J., Zhan Z.J., Sun L.L., Zhang J., and Wang W.K.: Wear behavior of bulk Zr41Ti14Cu12.5Ni10Be22.5 metallic glass. J. Mater. Res. 17, 1877 (2002).
9Blau P.J.: Friction and wear of a Zr-based amorphous alloy under dry and lubricated conditions. Wear 250, 431 (2001).
10Fu X., Kasai T., Falk M.L., and Rigney D.A.: Sliding behavior of metallic glass: Part I. Experimental investigations. Wear 250, 409 (2001).
11Murali P. and Ramamurty U.: Embrittlement of a bulk metallic glass due to sub-Tg annealing. Acta Mater. 53, 1467 (2005).
12Ramamurty U., Lee I.M.L., Basu J., and Li Y.: Embrittlement of a bulk metallic glass due to low temperature annealing. Scripta Mater. 47, 107 (2002).
13Nagendra N., Ramamurty U., Goh T.T., and Li Y.: Effect of crystallinity on the impact toughness of a La-based bulk metallic glass. Acta Mater. 48, 2603 (2000).
14Basu J., Nagendra N., Li Y., and Ramamurty U.: Microstructure and mechanical properties of partially-crystallized la-based bulk metallic glass. Philos. Mag. 83, 1747 (2003).
15Oliver W.C. and Pharr G.M.: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564 (1992).
16Schuh C.A., Neih T.G., and Kawamura Y.: Rate dependence of serrated flow during nanoindentation of a bulk metallic glass. J. Mater. Res. 17, 1651 (2002).
17Schuh C.A., Lund A.C., and Nieh T.G.: New regime of homogeneous flow in the deformation map of metallic glasses: Elevated temperature nanoindentation experiments and mechanistic modeling. Acta Mater. 52, 5879 (2004).
18Greer A.L., Castellero A., Madge S.V., Walker I.T., and Wilde J.R.: Nanoindentation studies of shear banding in fully amorphous and partially devitrified metallic alloys. Mater. Sci. Eng., A 375–377, 1182 (2004).
19Van Den Beukel A. and Sietsma J.: The glass transition as a free volume related kinetic phenomenon. Acta Metall. Mater. 38, 383 (1990).
20Slipenyuk A. and Eckert J.: Correlation between enthalpy change and free volume reduction during structural relaxation of Zr55Cu30Al10Ni5 metallic glass. Scripta Mater. 50, 39 (2004).
21Patnaik M.N.M., Narasimhan R., and Ramamurty U.: Spherical indentation response of metallic glasses. Acta Mater. 52, 3335 (2004).
22Ramamurty U., Jana S., Kawamura Y., and Chattopadhyay K.: Hardness and plastic deformation in a bulk metallic glass. Acta Mater. 53, 705 (2005).
23Bhowmick R., Raghavan R., Chattopadhyay K., and Ramamurty U.: Plastic flow softening in a bulk metallic glass. Acta Mater. 54, 4221 (2006).
24Fu X., Falk M.L., and Rigney D.A.: Sliding behavior of metallic glass: Part II. Computer simulations. Wear 250, 420 (2001).
25Schuh C.A. and Neih T.G.: A survey of instrumented indentation studies on metallic glasses. J. Mater. Res. 19, 46 (2004).
26Sharmal S.K., Strunskus T., Ladebusch H., and Faupel F.: Surface oxidation of amorphous Zr65Cu17.5Ni10Al7.5 and Zr46.75Ti8.25Cu7.5Ni10Be27.5. Mater. Sci. Eng., A 304–306, 747 (2001).
27Wu Y., Nagase T., and Umakoshi Y.: Effect of crystallization behavior on the oxidation resistance of a Zr–Al–Cu metallic glass below the crystallization temperature. J. Non-Cryst. Solids 352, 3015 (2006).
28Paljevia M.: High-temperature oxidation behaviour in the Zr-Al system. J. Alloys Compd. 204, 119 (1994).
29Kai W., Hsieh H.H., Nieh T.G., and Kawamura Y.: Oxidation behavior of a Zr–Cu–Al–Ni amorphous alloy in air at 300–425 °C. Intermetallics 10, 1260 (2002).
Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Journal of Materials Research
  • ISSN: 0884-2914
  • EISSN: 2044-5326
  • URL: /core/journals/journal-of-materials-research
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords:

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 52 *
Loading metrics...

Abstract views

Total abstract views: 139 *
Loading metrics...

* Views captured on Cambridge Core between September 2016 - 24th October 2017. This data will be updated every 24 hours.