Weight loss behavior of a vacuum sintered powder metallurgical Fe–Mn–Si alloy

Published online by Cambridge University Press:  05 January 2017

Zhigang Xu
Affiliation:
Department of Chemical and Materials Engineering, University of Auckland, Auckland1142, New Zealand
Michael A. Hodgson
Affiliation:
Department of Chemical and Materials Engineering, University of Auckland, Auckland1142, New Zealand
Peng Cao*
Affiliation:
Department of Chemical and Materials Engineering, University of Auckland, Auckland1142, New Zealand
*
a)Address all correspondence to this author. e-mail: p.cao@auckland.ac.nz
Get access

Abstract

This work presents the effects of sintering temperature and mechanical milling on the weight loss of the powder metallurgical Fe–28Mn–3Si (wt%) alloy. Mechanically milled (MM) and blended elemental (BE) Fe–28Mn–3Si powder mixtures were prepared. Both the MM and BE compacts were sintered in a vacuum furnace for 3 h at various temperatures. It was found that weight loss occurred among all the sintered compacts. The weight loss of the sintered MM compacts was much lower than their BE counterparts sintered at the same temperature. The weight loss of the compacts was mainly caused by the sublimation of Mn in the Mn depletion region. A single α-Fe phase was observed on the surface of all the sintered samples. Predominant γ-austenite and minor ε-martensite were detected in all the sintered compacts at locations beyond the Mn depletion region. Mn3Si phase was found in BE alloys sintered at 1000 °C.

Type
Articles
Copyright
Copyright © Materials Research Society 2017 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

Contributing Editor: Jürgen Eckert

References

REFERENCES

Stanford, N. and Dunne, D.P.: Effect of Si on the reversibility of stress-induced martensite in Fe–Mn–Si shape memory alloys. Acta Mater. 58(20), 6752 (2010).CrossRefGoogle Scholar
Gebhardt, T., Music, D., Kossmann, D., Ekholm, M., Abrikosov, I.A., Vitos, L., and Schneider, J.M.: Elastic properties of fcc Fe–Mn–X (X = Al, Si) alloys studied by theory and experiment. Acta Mater. 59(8), 3145 (2011).CrossRefGoogle Scholar
Sato, A., Chishima, E., Yamaji, Y., and Mori, T.: Orientation and composition dependencies of shape memory effect in Fe–Mn–Si alloys. Acta Metall. 32(4), 539 (1984).CrossRefGoogle Scholar
Sato, A., Yamaji, Y., and Mori, T.: Physical properties controlling shape memory effect in Fe–Mn–Si alloys. Acta Metall. 34(2), 287 (1986).CrossRefGoogle Scholar
Koyama, M., Sawaguchi, T., and Tsuzaki, K.: Si content dependence on shape memory and tensile properties in Fe–Mn–Si–C alloys. Mater. Sci. Eng., A. 528(6), 2882 (2011).CrossRefGoogle Scholar
Xu, Z., Hodgson, M.A., and Cao, P.: A comparative study of powder metallurgical (PM) and wrought Fe–Mn–Si alloys. Mater. Sci. Eng., A. 630, 116 (2015).CrossRefGoogle Scholar
Liu, B., Zheng, Y., and Ruan, L.: In vitro investigation of Fe30Mn6Si shape memory alloy as potential biodegradable metallic material. Mater. Lett. 65(3), 540 (2011).CrossRefGoogle Scholar
Xu, Z., Hodgson, M.A., and Cao, P.: Microstructure and degradation behavior of forged Fe–Mn–Si alloys. Int. J. Mod. Phys. B. 29(11), 1540014-1 (2015).CrossRefGoogle Scholar
Miller, F.P., Vandome, A.F., and John, M.B.: Ellingham Diagram (VDM Publishing, Saarbrücken, Germany, 2010); pp. 180.Google Scholar
Šalak, A., Selecka, M., and Bureš, R.: Manganese in ferrous powder metallurgy. Powder Metall. Prog. 1(1), 41 (2001).Google Scholar
Hryha, E., Dudrova, E., and Nyborg, L.: Critical aspects of alloying of sintered steels with manganese. Metall. Mater. Trans. A 41(11), 2880 (2010).CrossRefGoogle Scholar
Hryha, E., Gierl, C., Nyborg, L., Danninger, H., and Dudrova, E.: Surface composition of the steel powders pre-alloyed with manganese. Appl. Surf. Sci. 256(12), 3946 (2010).CrossRefGoogle Scholar
Redlich, O. and Kister, A.: Algebraic representation of thermodynamic properties and the classification of solutions. Ind. Eng. Chem. 40(2), 345 (1948).CrossRefGoogle Scholar
Saunders, N. and Miodownik, A.P.: CALPHAD (Calculation of Phase Diagrams): A Comprehensive Guide: A Comprehensive Guide (Elsevier, Amsterdam, 1998).Google Scholar
Forsberg, A. and Ågren, J.: Thermodynamic evaluation of the Fe–Mn–Si system and the γ/ε martensitic transformation. J. Phase Equilib. 14(3), 354 (1993).CrossRefGoogle Scholar
Lide, D.R.: CRC Handbook of Physics and Chemistry, 88th ed. (CRC Press, Boca Raton, 2007); pp. 1135.Google Scholar
Jones, H.A. and Mackay, G.: The rates of evaporation and the vapor pressures of tungsten, molybdenum, platinum, nickel, iron, copper and silver. Phys. Rev. 30(2), 201 (1927).CrossRefGoogle Scholar
Langmuir, I.: Vapor pressures, evaporation, condensation and adsorption. J. Am. Chem. Soc. 54(7), 2798 (1932).CrossRefGoogle Scholar
Chen, G., Cao, P., He, Y., Shen, P., and Gao, H.: Effect of aluminium evaporation loss on pore characteristics of porous FeAl alloys produced by vacuum sintering. J. Mater. Sci. 47(3), 1244 (2012).CrossRefGoogle Scholar
Effenberg, G. and Ilyenko, S.: Iron Systems, Part 4: Selected Systems from Cu–Fe–Si to Fe–N–U (Springer Berlin-Heidelberg, Berlin, 2008); pp. 319358.Google Scholar
German, R.M.: Powder Metallurgy, and Particulate Materials Processing: The Processes, Materials, Products, Properties and Applications (Metal Powder Industries Federation, Princeton, 2005); pp. 221260.Google Scholar
Suryanarayana, C.: Mechanical alloying and milling. Prog. Mater. Sci. 46(1), 1184 (2001).CrossRefGoogle Scholar
Zheng, W., Lu, X-G., He, Y., Cui, Y., and Li, L.: Thermodynamic assessment of the Fe–Mn–Si system and atomic mobility of its fcc phase. J. Alloys Compd. 632, 661 (2015).CrossRefGoogle Scholar
Raghavan, V.: Phase Diagrams of Ternary Iron Alloys (Indian Institute of Metals, Delhi, India, 1988); pp. 363377.Google Scholar