Self-intercalation forms covalently bonded 2D transition metal chalcogenide layers
A research team led by Kian Ping Loh and Stephen J. Pennycook of the National University of Singapore, as well as Xin Luo of Sun Yat-sen University report a new class of metal chalcogenides, in their article published in Nature. These materials are transition metal dichalcogenide bilayers sandwiching metal atoms covalently.
The layered structure of metal dichalcogenides enables the synthesis of novel materials. Typically, two-dimensional metal dichalcogenides are composed of nanosheets stacked together, in analogy to graphene. Adjacent layers are held together via weak van der Waals force. The inter-layer spaces can host guest species, including atoms and ions. Previous works focused primarily on introducing foreign ions or atoms within a single metal-chalcogenide layer, “but somehow, previous researchers missed considering the situation when the same metal atoms sit in between two layers,” says Xiaoxu Zhao, the lead author. The researchers decided to step into this unexplored area.
The research team modified the synthesis protocols involving molecular beam epitaxy (MBE) for synthesizing metal dichalcogenides. MBE is a gas-phase technique for growing highly uniform and crystalline thin films. The key to the synthesis of a new family of metal chalcogenides is to enhance the concentration of gaseous metal precursors intentionally. During the thin-film deposition, the additional metal atoms reside in the interstitial space between the as-formed metal dichalcogenide monolayers and formed covalent bonds with neighboring layers. For example, increasing the Ta:S flux ratio from 1:10 (which formed conventional metal dichalcogenide, TaS2.) to 1:6 resulted in Ta-intercalated tantalum disulfide, Ta7S12. Changing the flux ratio was found to tune the stoichiometry to obtain other compounds, for example, Ta9S16 and Ta10S16. Additionally, this strategy is also applicable to chemical vapor deposition, another common synthesis technique of metal dichalcogenides.
In some cases, the newly synthesized metal chalcogenides possess magnetic properties that their corresponding monolayer counterparts lack. The intercalated metal atoms located in the interstitial sites in the inter-layer space can transfer electrons to the host layers, altering the electronic structure of the metal chalcogenides, rendering different magnetic behaviors. For instance, the newly synthesized Ta7S12 is ferromagnetic, whereas its parental compound, TaS2, is non-ferromagnetic.
Babak Anasori of Indiana University–Purdue University Indianapolis believes that “adding covalent bonds between the flakes of transition metal dichalcogenides will lead to new compounds with the large available compositional space while keeping the thickness at the ultrathin nanometer levels. This strategy might [unveil] novel properties, including room-temperature, ambient-stable two-dimensional ferromagnets.” Anasori was not involved in this study.
Significantly, density functional theory predicts that besides Ta and S, transition metals of V, Cr, Mn, and Te, along with VI-A elements of S, Se, and Te, are feasible elements constituting the self-intercalated chalcogenides. Zhao says, “Owing to the versatility in the composition control, it is possible to tune, in one class of materials, properties that can vary from ferromagnetic to non-ferromagnetic and spin-frustrated Kagome lattices. This discovery presents a rich landscape of ultrathin three-dimensional materials that await the further discovery of new properties.”
Read the abstract in Nature.