In this work a new generation of periodic mesoporous organosilica (PMO) low-k dielectrics with targeted k-values 2.0 and 1.8 is evaluated. In addition, impact of two different curing processes on properties of the mesoporous material is analyzed. It is shown that removal of templating organics with thermal annealing leads to formation of mechanically robust and chemically very stable material, while application of UV-assisted curing with broadband lamp (λ > 200 nm) causes pronounced decrease of film ability to sustain in diluted HF solution. The explanation of that phenomenon is given in terms of silica-ring structures formed within organosilica skeleton.

Dry-coated nanosilver is a promising material for bio-applications. Its inert and non-porous nanothin SiO2 coating preserves the plasmonic properties of the nanosilver and cures its toxicity by (1) preventing direct cell to silver contact and (2) blocking the release of toxic silver ions. However, fully hermetic coatings have, to date, not been produced. During the coating process, a certain number of core particles are either coated only partially, or escape the coating process entirely. Here, a systematic parametric study was undertaken in order to optimize an aerosol reactor for the synthesis and dry-coating of nanosilver. The reactor was optimized with respect to coating injection height, jet number, mixing flow rate. By synthesizing xAg/SiO2 composite particles, small silver sizes (9-11 nm) with relatively high Ag ion release were obtained. This enabled the quantitative evaluation of the coatings by Ag ion release measurements.

The ‘DLC-GFET’, a graphene field effect transistor with a diamondlike carbon (DLC) top-gate dielectric film, is presented. The DLC film was formed ‘directly’ onto the graphene channel without forming passivation interlayers using our original photoemission-assisted plasma-enhanced chemical vapor deposition (PA-CVD), where the plasma was precisely controlled by photoemission from the sample with quite low electric power to minimize plasma damage to the channel. The DLC-GFET exhibits clear ambipolar characteristics with a slightly positive shift of the neutral points (Dirac voltages). Relatively high transconductances were obtained as 14.6 (8.8) mS/mm in the n (p) channel modes, respectively, with a thick gate dielectric of 48 nm and a long gate length of 5 μm, promising vertical scaling-down to improve the high-frequency performance. The positive shift of the Dirac voltage is due to unintentional hole doping from oxygen species in the DLC film into the graphene channel, promising a minute modulation doped structure with oxygen to overcome high resistance in the access region. Hence, a DLC film deposited by PA-CVD is a candidate for the gate dielectric on graphene.

The aim of this research work is to study the effect of boron addition on mechanical properties and microstructure of a new family of low carbon NiCrVCu advanced high strength steels (AHSS). Experimental steels are thermo-mechanically processed (TMP) (hot-rolled+quenched). Results show that the microstructure of these steels contains bainite and martensite, predominantly, which nucleate along prior austenite grain boundaries (GB). On the other hand, tensile tests reveal that the TMP steels have YS (0.2% offset) of 978 MPa, UTS of 1140 MPa and EL of 18%. On the basis of exhibited microstructure and mechanical properties, these experimental steels are classified as bainitic-martensitic complex phase (CP) advanced ultra-high strength steels (UHSS).

The ability to control the deposition of mouse embryonic stem cells (mESCs),and mESCs encapsulated in 200-μm diameter alginate microbeads, intocustomized patterns has recently been achieved using laser direct-write(LDW). Gelatin-based LDW was utilized to target and reproducibly depositgroups of cells directly onto receiving substrate surfaces. Live/deadstaining for cell viability and immunocytochemistry for the pluripotencymarker, Oct-4, indicated that transferred mESCs were viable followingtransfer, and maintained an important embryonic stem cell marker,respectively. LDW was further used to print mESCs encapsulated in hydrogelmicrobeads into customized patterns on a single-bead basis. Recent effortshave also achieved patterns of discrete co-cultures of mESCs and breastcancer cells in separate hydrogel microbeads. Altogether, we demonstratedthe feasibility of LDW to print patterns of mESCs and mESC-microbeads forthe biomimetic assembly of engineered cellular constructs and tissuemodels.

This work presents a surface study of monolithic vitreous (or glassy) carbon - MVC - obtained from vitreous carbon powder. Defective MVC pieces are crushed in a ball mill and size classified by sifting. The MVC powder is mixed with furfuryl-alcohol resin and compacted in a mould using a hydraulic press. Samples with different powder granulometries are produced in this way and carbonized in a furnace under nitrogen atmosphere. Complete carbonization of the “powder” is achieved in only one day and losses due to breakage of the pieces is less than 5%. These results compare very favorably with respect to traditional MVC production methods where full carbonization may require up to seven days and losses due to breakage can be as high as 70%. After carbonization, samples are sanded and polished. Surface roughness and microstructure are characterized by light microscopy. Porosity is quantified from micrographs using ImageJ software and nanometric height variations are measured by atomic force microscopy.

In this work, reactive magnetron-sputtered Pb(Zr,Ti)O3thin films were used to fabricate well-ordered nanodot arrays by means of nanosphere lithography (NSL). NSL is based on a two-step etch process by means of, firstly adjusting the diameter of polystyrene spheres in the self-assembled polymeric nanosphere mask using reactive ion etching, and secondly transferring the mask to the substrate by ion milling with adjusted heights. Hence, structures with different aspect ratios can be fabricated.

Piezoresponse force microscopy was used as the inspection tool on both non-patterned and patterned films. Both the topography and polarization out of plane and in plane was deduced in this mode. Grains of nanodots with low aspect ratio form domain structures comparable to domains in non-patterned films. In contrast to that, nanodots with a higher aspect ratio form particular structures. The in-plane amplitude images show mostly a bisectioned domain assembly, while the out-of-plane amplitude images show in some cases more complex structures like “c”-shaped domains or multi-domains around a center domain.

The patterning of the ferroelectric material was shown to affect the formation of ferroelectric domains. The initial polycrystalline, randomly-ordered films are re-oriented and show domain structures depending on nanodisc diameter and aspect ratio. This may enable tailoring of ferroelectric materials in their piezoelectric and pyroelectric properties by patterning.

Ferroelectric 0.7BiFeO3-0.3PbTiO3 (BFO-PT) films were deposited on stainless steel substrates by the sol-gel method. A thin layer of PbTiO3 (PT) was introduced between the substrates and BFO-PT films in order to decrease the annealing temperature of BFO-PT films. X-ray diffraction analysis reveals that BFO-PT films could be well crystallized into the perovskite structure at about 575 oC. Scanning electron microscope (SEM) images show that BFO-PT thin films have grain size of about 50∼60 nm. Our results indicated BFO-PT films deposited on stainless steel substrates maintained the excellent ferroelectric properties with remnant polarization of about 40∼50 μC/cm2.

Nanotribology, the study of friction, wear and lubrication at the nanoscale is an important area of research; however in practice due to the size scale, requires specifically designed tools to characterize nanoscale contacts. We have developed a TEM triboprobe incorporating an advanced nano-positioner with 3D programmable motion inside a transmission electron microscope (TEM) which allows us to selectively apply multiple reciprocating wear cycles to a nanoscale surface, and observe in real-time dynamical changes and the evolution of wear around a sliding nano-contact.

Nanoscale cyclic rubbing of an automotive aluminum-silicon alloy processed by focused ion beam (FIB) reveals dynamical surface fragmentation and the generation of nanoscale debris particles. The nanoparticles undergo complex motion as they interact with the sliding nano-contact. Over hundreds of reciprocating cycles, frictional heating leads to a phase separation of the Ga+ ions implanted by FIB forming liquid Ga nano-droplets and liquid bridges. The addition of nanoscale debris particles and liquid droplets dramatically changes the wear dynamics and transforms a 2-body sliding contact into a complex 4-body solid–liquid system exhibiting time-dependent, non-equilibrium kinetic behavior.

TEM nanotribology opens up new possibilities for the real-time quantification of cyclic friction, wear and dynamic solid–liquid nano-mechanics, which will have widespread applications in many areas of nano-science and nanotechnology.

Necessity of recognition of compound structures appears in different applications. Electrical tomography is one of perspective approach for investigation of material structures. A new special measurement scheme in electric tomography is proposed for the domain as a circle. This scheme opens possibility to construct electric tomography apparatus with faster computer recognition of structure of compounds materials, using General Ray algorithms. Computer simulation of this scheme is realised with MATLAB software and justified by numerical experiments on examples, related with electrical tomography.

Alloy 617, a high-temperature creep-resistant, nickel-based alloy, is being considered for the primary heat exchanger for the next generation nuclear plant, which is highly influenced by thermal creep. The main objective of this study is to inspect the crept grain boundaries under its imitated working condition, and to determine which boundaries are susceptible to damage and which are more resistant, in order to help improve its creep resistance in future manufacturing. Electron backscatter diffraction was used to measure the proportions of each boundary by observing and analyzing these crept microstructures. The grain-boundary distribution can be expressed in terms of five parameters including three parameters of lattice misorientation and two parameters of the grain-boundary plane normal. Three conditions were analyzed: the original material, metal that was annealed without stress, and ones that were crept at 1000ºC at 19 MPa and 25 MPa for various times. Though observation, it is found that the voids seldom occur at low angle grain boundaries, and coherent twin boundaries are also resist to creep damage.

Nanoindentation test is known as instrumented indentation test (IIT) in the nano range for hardness and material parameters (ISO14577). It is a simple and effective method for evaluating the mechanical properties such as elasticity/stiffness, hardness and adhesion. Generally IIT is the method that doesn’t have to observe the residual impression. However, it is necessary to observe the residual impression and surface of test piece to obtain the material behavior such as pile-up/sink-in, crack. In past work, the phase shifting interferometric scanning confocal microscope (PSISCM)-nanoindenataion combined system was developed to obtain the tilt of surface and the geometrical shape of residual impression that are deeper than one micron. This system is useful to obtain the geometrical shape of the surface of test piece in macro and micro range. However, it is well known that the results of nanoindentation test become unstable in the nano range.

In this work, authors focused the geometry observation system for nanoindentation system. Confirmation the capability of PSISCM system and development of objective type atomic force microscopy to obtain the geometrical shape in nano range are examined. The AFM that has an excellent performance is developed by SII nanotechnology Inc. Japan, and it built into system. In many cases, it performs enough to observe the residual impression and the surface of the test piece. This system uses three methods to obtain the geometrical shape of surface in each range. Generally, AFM has the observation range at about several microns. It is difficult to search the small residual impression by only AFM. Before the observation of AFM, the observation area should be selected by using PSISCM. New measurement tool using PSISCM and AFM to obtain the surface geometry from macro range to nano range is proposed. This tool is very simple, quick and useful tool.

We report the results of using n-type hydrogenated nanocrystalline silicon oxide alloy (nc-SiOx:H) in hydrogenated nanocrystalline silicon (nc-Si:H) and amorphous silicon germanium alloy (a-SiGe:H) single-junction solar cells. We used VHF glow discharge to deposit nc-SiOx:H layers on various substrates for material characterizations. We also used VHF glow discharge to deposit the intrinsic layer in nc-Si:H solar cells. RF glow discharge was used for the deposition of the doped layers and the intrinsic layer in a-SiGe:H solar cells. Various substrates such as stainless steel (SS), Ag coated SS, and ZnO/Ag coated SS were used for different cell structures. We found that by using nc-SiOx:H to replace the ZnO and the a-Si:H n-layer in nc-Si:H solar cells, the cell structure is greatly simplified, while the cell performances remain nearly identical to those made using the conventional n-i-p structure on standard ZnO/Ag BR’s. Solar cells with nc-SiOx:H as the n layer directly deposited on textured Ag show similar quantum efficiency (QE) as the n-i-p cells on ZnO/Ag BRs. In both cases, QE is higher than that in the n-i-p cells made directly on Ag coated SS. This effect is probably caused by the shift of surface plasmon-polariton resonance frequency due to the difference in index of refraction of ZnO, nc-SiOx:H, and Si.

We propose plasmonic platform that can enable optical trapping, spectroscopy and biosensing, all in the same platform. The system is based on periodic arrays of gold nanopillars fabricated on a supporting gold layer. The proposed platform is highly desirable for biosensing applications since it supports highly refractive index sensitivities as large as 675 nm/RIU which. The spectrally sharp resonances provides large figure of merits as large as 112.5. As the nanopillar array supports large near-field intensities accessible to the biomolecules in the sample around the platform, as large as 10.000 times, the proposed structure can be used for surface enhanced spectroscopy applications. The pillar array also supports plasmonic hot spots with high near-field intensity gradient leading to large gradient forces, 350 pN/W/μm2 which is needed for optical trapping applications.

Hydrogen fluoride (HF) is a known product from the combustion or detonation of explosives formulated with fluoropolymer binder systems. This presents the user with elevated risk levels, particularly during unintended combustion events or detonations in close combat situations. In an effort to remediate the production of HF, calcium disilicide was added to explosive formulations in an effort to decrease the amount of HF formed. First, VitonA/calcium disilicide mixtures were made and the thermal decomposition characteristics studied using thermal gravimetric/differential thermal analysis. The activation energy ranged from approximately 145-190 kJ/mol, indicative of C-F scission in the Viton binder prior to calcium fluoride formation. An energetic formulation was made which consisted of approximately a 5/3 mass ratio of Viton/CaSi2. Combustion calorimetry in oxygen and air and subsequent analysis of the residues using x-ray diffraction (XRD) and energy dispersive x-ray analysis (EDS) revealed that calcium fluoride formed. The amount of HF reduced was determined by trapping off gases in a cooling loop, rinsing into water, and analysis in anion exchange chromatography. Upon introduction of calcium disilicide into the formulation, a ~30% decrease in HF formation was observed along with appearance of CaF2 and free Si in the residue. Such products are consistent with the mechanism following a general decomposition path of 2F + CaSi2→CaF2+2Si. The same formulation was detonated, and upon product analysis it was determined the decomposition path followed nearly the same route with a net decrease in HF formation, but with a portion of the silicon oxidizing slightly further to SiO2.

Within the framework of a grand partition function formalism, we examine the occupancy of the dangling bond dislocation defect sites and the VGa-ON dislocation defect sites within uncompensated n-type gallium nitride. The sensitivity of these results to variations in the unoccupied dislocation defect energy level is examined. We find that the VGa-ON dislocation defect sites’ greater capacity to store charge plays a large role in influencing the results, i.e., greater free electron and bulk donor concentrations are required in order to fully saturate the threading dislocation lines with charge.

Vertical-Cavity Surface-Emitting Lasers are making up a large and growing share of the world’s production of semiconductor lasers. But the 850 nm GaAs quantum well VCSELs that make up most of present product are highly vulnerable to dislocation networks. In this paper, we discuss how materials selection affects the reliability of semiconductor lasers generally. We then describe the most common failure mechanisms observed in VCSELs, and what precautions are used to prevent them. We finish with a brief discussion of reliability testing and failure analysis.

Focused ion beam (FIB) milling coupled with scanning electron microscopy (SEM) on the same platform enables 3D microstructural analysis of structures using FIB for serial sectioning and SEM for imaging. Since FIB milling is a destructive technique, the acquisition of multiple signals from each slice is desirable. The feasibility of collecting both an inlens backscattered electron (BSE) signal and an inlens secondary electron (SE) simultaneously from a single scan of the electron beam from each FIB slice is demonstrated. The simultaneous acquisition of two different SE signals from two different detectors (inlens vs. Everhart-Thornley (ET) detector) is also possible. Obtaining multiple signals from each FIB slice with one scan increases the acquisition throughput. In addition, optimization of microstructural and morphological information from the target is achieved using multi-signals. Examples of multi-signal FIB/SEM tomography from a dental implant will be provided where both material contrast from the bone/ceramic coating/Ti substrate phases and porosity in the ceramic coating will be characterized.

Compressibility of anatase nano particles of TiO2 changes from the bulk counterpart. This has been associated with amorphization and compaction. The behavior of such systems under extreme conditions is examined using a shell partial distribution function and some comparison made with rutile and baddeylite polytypes based nano structures. Particle energies of rutile and baddeylite nano particles appear to be rather size independent as compared to the anatase polytypes. The latter is associated with large relaxations and re-bonding in the relatively soft anatase phase of nano TiO2.

Creation of nanoscale building blocks with various sizes and shapes are critical for the progress of nanotechnology. Silicon carbide nanostructures attract interest due to their applications in optoelectronic devices, sensors, high-power/high temperature electronics, and thermoelectrics. This paper presents a detailed study of SiC nanowire morphology change through gas flow dynamics. SiC nanowire synthesis has been carried out by chemical vapor deposition using hexamethyldisilane (HMDS) as source material on SiO2/Si substrate. The study has been limited to several catalyst materials, including nickel (nanoparticle and thin film), cobalt nanoparticles, and gold thin film. The growth runs have been carried out at 1000oC under H2 as carrier gas with flow rates varying from 100 to1000 sccm. A significant change in morphology has been observed. At high flow rates, the nanowires are highly curved and contain sharp kinks, while the nanowires are straight and longer at lower flow rates. Moreover, it is important to note that the flow rate has influenced the nanowire growth-yield significantly. As small as 8nm-diameter SiC nanowire has been observed, as determined by transmission electron microscopy (TEM). These findings will help in controlling the morphology of the SiC nanowires. The fabricated nanowires have also been characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR).