A de novo drug delivery nanosystem based on gold nanoparticles (GNPs), decorated poly(ethylene glycol) (PEG), and folate (FA)-conjugated graphene oxide (GO) was designed and developed successfully. Initially, the graphite (G) powder was oxidized to the GO, and then functionalized with chloroacetic acid to afford a carboxylated graphene oxide (GO–COOH). The obtained GO–COOH was functionalized with an amine end-caped PEG, FA, as well as 3-amino-1-propanethiol to produce a GO–PEG–FA–SH. In another experimental section, GNPs were synthesized through a citrate-mediated reduction approach, and subsequently decorated onto/into GO–PEG–FA–SH through the formation of Au–S bond to afford a GO–PEG–FA/GNP nanosystem. The resultant nanosystem was loaded with doxorubicin hydrochloride (DOX) as a model anticancer drug, and its drug-loading capacity as well as pH-dependent drug release behavior were investigated. The anticancer activity of the developed theranostic nanomedicine was extensively evaluated using MTT assay against human breast cancer cells (MCF7). The developed GO–PEG–FA/GNPs–DOX theranostic nanomedicine exhibited an excellent cancer chemotherapy feature. In addition, this nanomedicine can be used in chemo-photothermal therapy of solid tumors because of the presence of GO and GNPs in its structure.

Effective cancer therapy is usually limited by the off target distribution of chemotherapeutic drugs and multidrug resistance (MDR) of cancer cells. As a result, the development of a drug delivery system (DDS) capable of targeting cancer cells while at the same time delivering two or more chemotherapeutic drugs is believed to be a good solution to this dilemma. Herein, a hyaluronan-coated meta-organic framework nanoparticles (HM) were fabricated as a DDS in our study to deliver cisplatin (PDD) and oleanolic acid (Ola). Positive results were obtained in our study which reveal that the DDS (HM/PDD/Ola) is favorable in colorectal cancer (HCT116) therapy by enhancing targeted apoptosis and reversing MDR. Compared with applying free drugs or mono DDS, the dual loaded HM/PDD/Ola showed synergistic effects and better performance, which might be a future alternative for the chemotherapy of colorectal cancer.

Regarding the effect of composition on the mechanical properties of intermetallic phases such as Laves phases, there is conflicting information in the literature. Some authors observed defect hardening when deviating from stoichiometric Laves phase composition, whereas others find defect softening. Here, we present a systematic investigation of the defect state, hardness, and elastic modulus of cubic and hexagonal NbCo2 Laves phases as a function of crystal structure and composition. For this purpose, diffusion couples were prepared which exhibit diffusion layers of the cubic C15 and hexagonal C14 and C36 NbCo2 Laves phases, with concentration gradients covering their entire homogeneity ranges from 24 to 37 at.% Nb. Direct observations of dislocations and stacking faults in the diffusion layers as a function of composition were performed by electron channeling contrast imaging, and the hardness and elastic modulus were probed in the diffusion layers along the concentration gradients by nanoindentation.

In this work, four N-TiO2/bismuth oxyiodide (BiOI)/reduced graphene oxide (RGO) composite photocatalysts with different composite ratios were prepared using a hydrothermal method. The phase, surface structure, specific surface area, and light response were characterized by X-ray diffraction, X-ray photoelectron spectrum analysis, scanning electron microscopy, specific surface area and aperture analysis, and UV-vis diffuse reflection spectrum analysis. The results indicated that the N-TiO2/BiOI/RGO (NTGB) composite prepared with a mass ratio of 1:1:2 is a promising photocatalyst for the degradation of organic pollutants by using sunlight, with a specific surface area of 139.56 (m2/g), bandgap of 1.24 eV, and strong absorption with a smaller visible region. It has the best photocatalytic properties under visible light irradiation in the degradation of methylene blue (MB): the degradation rate of MB in the presence of light for 60 min reached 99.22%, and its photocatalytic performance was significantly higher than that of TiO2, N-TiO2, BiOI, N-TiO2/BiOI, BiOI/RGO, NTGB1, NTGB2, and NTGB4.

Using evanescent wave (EW)–based optical detection methods coupled with video microscopy, we investigated in situ trajectories, diffusion, and interaction energies of ∼140 nm ceria particles near a glass surface at pH 3, 5, and 7. Trajectories of a single ceria particle in a 2D (x–y) plane were obtained by linking its time-sequenced positions. Diffusion coefficients of several single ceria particles were calculated from their respective mean-square displacement (MSD) versus time curves, and the results were interpreted based on the interaction potential energy curves obtained from Boltzmann statistics of the EW scattering intensity fluctuations of the particles. The types and characteristics of particle motions were determined by analyzing the MSD curves. Whereas both confined or subdiffusive and Brownian motions of the particles were observed at pH 7, only confined motion was seen at pH 3 and 5, and their corresponding diffusion coefficients are similar to those reported by several authors.

In this study, the magnetic properties of Fe39.8Co19.92Mn20.52Cr14.77Si5 multi-principal element alloy in both bulk and thin films were studied. X-ray diffraction measurements show coexisting face centered cubic (FCC) and hexagonal close packed phases in the bulk and the 500 nm thin films, while only FCC phase is observed in the 65 nm thin film. A four orders of magnitude increase in the magnetic moment is observed for 65 nm thin film compared with the bulk sample. Evolution of magnetization as a function of temperature and applied magnetic field shows multiple magnetic transitions. A paramagnetic to spin glass transition is detected at TS ∼ 390 K for all samples. Further cooling results in a spin glass to ferromagnetic (FM) transition, and the transition temperature, TF, is dependent on the film thickness. Higher saturation magnetization and transition temperature observed for the thin film samples indicate the stabilization of FM ordering due to thickness confinement.

Pop-in during indentation testing is a term used to indicate the sudden displacement burst during loading. Experimental data are measured during an indentation pop-in event, using displacement sensors with 20 μs time constant at 100 kHz data acquisition rate. The load–depth response during the pop-in event that occurs within 160 μs is determined after accounting for the instruments' dynamic response. Unlike the response reported in the literature for force-controlled tests, wherein the load on the sample remains constant during the pop-in, a steep load drop is observed after the onset of pop-in, followed by a significant increase in the load well beyond the load at the onset of pop-in. A model for the material and instrument's dynamic response is presented that agrees well with the experimental observations. The implications of these findings for determination of pop-in length or velocity and for performing displacement-controlled testing involving closed loop control are discussed.

SmTaO4 ceramics have excellent high-temperature phase stabilities and mechanical properties and show great potential for use as next-generation thermal barrier coating (TBC) materials. CeO2–SmTaO4 ceramics are prepared via high-temperature solid–state reaction. It retains a single monoclinic phase structure. Ce4+ was reduced to Ce3+ by high-temperature deoxidation, and the Ce3+ ions substitute for an equal number of Sm3+ ions. The CeO2–SmTaO4 ceramics had lower thermal conductivities [1.09–2.75 W/(m K)] than yttria-stabilized zirconia (YSZ) [2.1–2.7 W/(m K)] at 100–800 °C, which decreased dramatically with increasing temperature. SmTaO4 doped with 2% CeO2 had lower thermal conductivity [1.09 W/(m K), 800 °C] than SmTaO4 [1.42 W/(m K), 800 °C] and 2% ZrO2-doped SmTaO4 ceramics [1.22 W/(m K), 800 °C]. The low thermal conductivity is attributed to Ce3+ substitution for an equal number of Sm3+ ions, and because Ce3+ ions are the strongest phonon scattering centers, they can decrease the phonon mean free path effectively. The thermal expansion coefficient of 8% CeO2–SmTaO4 ceramics is approximately 10.3 × 10−6 K−1 at 1200 °C, which is slightly higher than that of both YSZ (10.0 × 10−6 K−1) and SmTaO4 (9.58 × 10−6 K−1). The outstanding thermophysical properties indicate that CeO2–SmTaO4 ceramics are potential TBC materials.

Materials with crystal structures containing tetrahedral motifs are preferable for optoelectronic applications because they often have direct band gaps and low electron effective masses. However, crystal structures of manganese chalcogenides typically contain octahedral motifs, such as in rock salt (RS) MnS and MnSe materials. Here, we experimentally show that MnS1−xSex alloys with tetrahedrally bonded wurtzite (WZ) structure can form between MnSe and MnS parent compounds with octahedral RS structures, at S-rich compositions (x < 0.4) and low synthesis temperatures (∼300 °C). The calculated mixing enthalpies of MnS1−xSex alloys in RS and WZ structures cannot explain this experimental observation, so we hypothesize that WZ stabilization may be related to smaller structure density and lower surface energy compared with RS. The resulting WZ MnS1−xSex alloys have 3.0–3.2 eV optical absorption onset and lower electrical conductivity (<0.0001 S/cm) than the parent RS compounds. These experimental measurement results are consistent with computationally predicted band gaps and effective masses.

The field of two-dimensional (2D) materials remains a key area of scientific research today, generating continual interest for electronic, sensing, and quantum technology. As the field progresses beyond proof-of-concept devices, experimental and analytical methods and results must be scrutinized to ensure the veracity of scientific claims. Here, some favored synthesis and characterization techniques within the 2D material (2DM) community and certain limitations inherent to these techniques are discussed. The authors highlight select caveats of solid-source and seed-promoted synthesis techniques, such as difficulties in reproducibility and compromised electrical performance of films synthesized with nucleation agents. Furthermore, the importance of careful characterization methodology in determining 2DM layer number, stoichiometry, and dopant effects is discussed. This article is intended to further educate researchers regarding select techniques and claims in the 2DMs field.

Osteoporosis is a skeletal disease characterized by bone loss and bone microarchitectural deterioration. The combination of smart materials and stem cells represents a new therapeutic approach. In the present study, highly porous scaffolds are prepared by combining the conducting polymer PEDOT:PSS with collagen type I, the most abundant protein in bone. The inclusion of collagen proves to be an effective way to modulate their mechanical properties and it induces an increase in scaffolds’ electrochemical impedance. The biomimetic scaffolds support neural crest-derived stem cell osteogenic differentiation, with no need for scaffold pre-conditioning contrarily to other reports.